Elektro-Isola G-Etronax SI Silicone, Glass Fabric Reinforcement, White, Sheets

Category	Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled
Manufacturer	Elektro-Isola
Trade Name	G-Etronax
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Elektro-Isola G-Etronax SI Silicone, Glass Fabric Reinforcement, White, Sheets.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Electrical and electrotechnical applications. Suitable as high-frequency insulation on account of its dielectric loss. Used as, among other things, an insulation material in large induction furnaces for smelting metal. Can be used as material for lampshades in thicknesses under 0.4 mm on account of the material’s great flexibility, high heat resistance and color stability.Information provided by Elektro-Isola

Physical Properties	Metric	English	Comments
Density	1.90 g/cc	0.0686 lb/in³	24hr/23°C/50% RH; ISO 1183-A; IEC/EN 60893-2 8.1
Water Absorption	0.16 %	0.16 %	24hr/50°C+24hr in water at 23°C,Test Specimen 50x50x3[mm]; ISO 62-1; IEC/EN 60893-2 8.2

Mechanical Properties	Metric	English	Comments
Tensile Strength	160 MPa @Thickness >=1.50 mm	23200 psi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6
Modulus of Elasticity	13.0 GPa @Thickness >=1.50 mm	1890 ksi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2
Flexural Strength	135 MPa @Thickness >=1.50 mm	19600 psi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1
	30.0 MPa @Treatment Temp. 200 °C, Time 3600 sec	4350 psi @Treatment Temp. 392 °F, Time 1.00 hour	ISO 178; IEC/EN 60893-2 5.1
	40.0 MPa @Treatment Temp. 250 °C, Time 3600 sec	5800 psi @Treatment Temp. 482 °F, Time 1.00 hour	ISO 178; IEC/EN 60893-2 5.1
	40.0 MPa @Treatment Temp. 150 °C, Time 3600 sec	5800 psi @Treatment Temp. 302 °F, Time 1.00 hour	ISO 178; IEC/EN 60893-2 5.1
	60.0 MPa @Treatment Temp. 100 °C, Time 3600 sec	8700 psi @Treatment Temp. 212 °F, Time 1.00 hour	ISO 178; IEC/EN 60893-2 5.1
	100 MPa @Treatment Temp. 50.0 °C, Time 3600 sec	14500 psi @Treatment Temp. 122 °F, Time 1.00 hour	ISO 178; IEC/EN 60893-2 5.1
	140 MPa @Treatment Temp. 20.0 °C, Time 3600 sec	20300 psi @Treatment Temp. 68.0 °F, Time 1.00 hour	ISO 178; IEC/EN 60893-2 5.1
Compressive Strength	330 MPa @Thickness >=5.00 mm	47900 psi @Thickness >=0.197 in	24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3
	110 MPa @Treatment Temp. 250 °C, Time 3600 sec	16000 psi @Treatment Temp. 482 °F, Time 1.00 hour	ISO 604; IEC/EN 60893-2 5.3
	150 MPa @Treatment Temp. 200 °C, Time 3600 sec	21800 psi @Treatment Temp. 392 °F, Time 1.00 hour	ISO 604; IEC/EN 60893-2 5.3
	230 MPa @Treatment Temp. 150 °C, Time 3600 sec	33400 psi @Treatment Temp. 302 °F, Time 1.00 hour	ISO 604; IEC/EN 60893-2 5.3
	270 MPa @Treatment Temp. 100 °C, Time 3600 sec	39200 psi @Treatment Temp. 212 °F, Time 1.00 hour	ISO 604; IEC/EN 60893-2 5.3
	310 MPa @Treatment Temp. 50.0 °C, Time 3600 sec	45000 psi @Treatment Temp. 122 °F, Time 1.00 hour	ISO 604; IEC/EN 60893-2 5.3
	330 MPa @Treatment Temp. 20.0 °C, Time 3600 sec	47900 psi @Treatment Temp. 68.0 °F, Time 1.00 hour	ISO 604; IEC/EN 60893-2 5.3
Shear Strength	15.0 MPa @Thickness >=5.00 mm	2180 psi @Thickness >=0.197 in	24hr/23°C/50% RH; IEC/EN 60893-2 5.5
Izod Impact, Notched (ISO)	45.0 kJ/m² @Thickness >=5.00 mm	21.4 ft-lb/in² @Thickness >=0.197 in	24hr/23°C/50% RH; ISO 180/2A; IEC/EN 60893-2 5.4.3

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Inert	210 °C @Thickness 0.000 mm, Time 7.20e+7 sec	410 °F @Thickness 0.000 in, Time 20000 hour	IEC 60216; IEC/EN 60893-2 7.1
Flammability, UL94	V-0	V-0	IEC/EN 60893-2 7.2; IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Insulation Resistance	1.00e+11 ohm @Thickness >=3.00 mm	1.00e+11 ohm @Thickness >=0.118 in	24hr/50°C+24h in water at 23°C; IEC 60167; IEC/EN 60893-2 6.3
Dielectric Constant	4.0 @Thickness <=3.00 mm, Frequency 50.0 Hz	4.0 @Thickness <=0.118 in, Frequency 50.0 Hz	96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
	4.0 @Thickness <=3.00 mm, Frequency 1.00e+6 Hz	4.0 @Thickness <=0.118 in, Frequency 1.00e+6 Hz	96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
Dielectric Strength	2.00 kV/mm @Thickness >=3.00 mm	50.8 kV/in @Thickness >=0.118 in	24hr/23°C/50% RH+1hr/oil 90°C; Parallel; IEC 60245-1; IEC/EN 60893-2 6.1.3.2
	7.00 kV/mm @Thickness 3.00 mm	178 kV/in @Thickness 0.118 in	24hr/23°C/50% RH+1hr/oil 90°C; Perpendicular; IEC 60245-1; IEC/EN 60893-2 6.1.3.1
Dissipation Factor	0.0030 @Frequency 50.0 Hz	0.0030 @Frequency 50.0 Hz	96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
	0.0030 @Frequency 1.00e+6 Hz	0.0030 @Frequency 1.00e+6 Hz	96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
Comparative Tracking Index	400 V @Thickness 3.00 mm	400 V @Thickness 0.118 in	IEC 60112; IEC/EN 60893-2 6.4