ATI Wah Chang 425™ Titanium Alloy, Hot Rolled & Annealed Plate

Category	Metal , Nonferrous Metal , Titanium Alloy
Manufacturer	ATI Wah Chang
Trade Name	425™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ATI Wah Chang 425™ Titanium Alloy, Hot Rolled & Annealed Plate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

ATI 425™ titanium is an innovative high strength alloy that has strength comparable to Ti-6-4, yet has the advantage that it can be cold worked. Originally developed for armor plate for ballistic protection, it was observed during processing to have exceptional hot workability. ATI 425™ titanium is an alpha-beta alloy that utilizes iron in place of some higher-cost vanadium as a beta stabilizer. Information provided by ATI Wah Chang

Physical Properties	Metric	English	Comments
Density	4.48 g/cc	0.162 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell C	32 - 36	32 - 36
Tensile Strength, Ultimate	965 MPa	140000 psi	Long.
	1010 MPa	146000 psi	Trans.
Tensile Strength, Yield	876 MPa	127000 psi	Long.
	924 MPa	134000 psi	Trans.
Elongation at Break	16 %	16 %	Long.
	16 %	16 %	Trans.
Modulus of Elasticity	114 GPa	16500 ksi	Long.
	119 GPa	17300 ksi	Trans.
Fracture Toughness	60.0 - 84.6 MPa-m½	54.6 - 77.0 ksi-in½

Thermal Properties	Metric	English
Melting Point	1600 - 1650 °C	2910 - 3000 °F
Solidus	1600 °C	2910 °F
Liquidus	1650 °C	3000 °F
Beta Transus	957 - 971 °C	1750 - 1780 °F

Component Elements Properties	Metric	English
Aluminum, Al	4.0 %	4.0 %
Iron, Fe	1.5 %	1.5 %
O2	0.25 %	0.25 %
Titanium, Ti	91.75 %	91.75 %
Vanadium, V	2.5 %	2.5 %

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.000154 ohm-cm	0.000154 ohm-cm