- ATI Allvac® Vasco® X-2M Specialty Steel, Heat Treatment: 899°C (1650°F) Normalization
ATI Allvac® Vasco® X-2M Specialty Steel, Heat Treatment: 899°C (1650°F) Normalization
| Category | Metal , Ferrous Metal |
| Manufacturer | ATI Allvac |
| Trade Name | Vasco® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ATI Allvac® Vasco® X-2M Specialty Steel, Heat Treatment: 899°C (1650°F) Normalization.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Allvac.Applications: High performance helicopter transmission gears, components.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.75 g/cc | 0.280 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C value for Brinell test with 3000 kg load/10 mm diameter ball |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C value. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C value. |
| Tensile Strength, Ultimate | 1207 MPa | 175100 psi | |
| Tensile Strength, Yield | 1138 MPa @Strain 0.200 % |
165100 psi @Strain 0.200 % |
|
| Elongation at Break | 16 % | 16 % | |
| Reduction of Area | 55 % | 55 % |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.15 % | 0.15 % | |
| Chromium, Cr | 5.0 % | 5.0 % | |
| Iron, Fe | 92 % | 92 % | as balance |
| Manganese, Mn | 0.50 % | 0.50 % | |
| Molybdenum, Mo | 1.4 % | 1.4 % | |
| Silicon, Si | 0.90 % | 0.90 % | |
| Vanadium, V | 0.50 % | 0.50 % |
Users viewing this material also viewed the following:
- Nyco 400 WOLLASTOCOAT® Wollastonite
- Termopol Termoton® K2GA4065A TPE Compound, based on SEBS and Polyolefins
- Sibur SKI-3S 1st Grade, 1st Group Isoprene Rubber (IR)
- United Cast Bar Unibar 350 Continuously Cast Iron
- ConocoPhillips ANDEROL® FGC 10 Synthetic Food Grade Compressor Fluid, ISO 32
- Akzo Nobel Expancel® 551 WE 80 d36 Wet expanded microspheres
- Beijing Chemical Industry KAIFA® 201-G15R PBT Resin
- BASF Sicotan® Yellow L 1912 Color Additive
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 60 PHR Iceberg Clay Filler
- Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), notched
Copyright © lookpolymers.com All Rights Reserved