ATI Allegheny Ludlum Martensitic Stainless Steel Type 420, Hardened + 482°C Temper

Category	Metal , Ferrous Metal , Stainless Steel , T 400 Series Stainless Steel
Manufacturer	ATI Allegheny Ludlum
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ATI Allegheny Ludlum Martensitic Stainless Steel Type 420, Hardened + 482°C Temper.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Allegheny Ludlum Type 420 is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainless steel. Oil quenching this alloy from temperatures between 1800°F and 1950°F produces the high strength and/or wear resistance as well as corrosion resistance.A major use for this grade of heat treatable stainless steels is in cutlery. When blanking cutlery parts from annealed raw material stock, Type 420 will usually exhibit hardness, yield strength, and tensile strength that are low enough for fine blanking purposes.UTS, TYS, and hardness values below obtained after austenitizing at 1800-1950°F (982-1066°C) followed by an oil quench and two hour temper as above.Information provided by Allegheny Ludlum Corporation.

Physical Properties	Metric	English	Comments
Density	7.73 g/cc	0.279 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell C	46	46
Tensile Strength, Ultimate	1606 MPa	232900 psi	Typical
Tensile Strength, Yield	1236 MPa @Strain 0.200 %	179300 psi @Strain 0.200 %	typical
Modulus of Elasticity	200 GPa	29000 ksi

Thermal Properties	Metric	English
CTE, linear	11.2 µm/m-°C @Temperature 20.0 - 200 °C	6.22 µin/in-°F @Temperature 68.0 - 392 °F
	12.5 µm/m-°C @Temperature 20.0 - 600 °C	6.94 µin/in-°F @Temperature 68.0 - 1110 °F
Thermal Conductivity	24.207 W/m-K @Temperature 100 °C	168.00 BTU-in/hr-ft²-°F @Temperature 212 °F
Melting Point	1454 - 1510 °C	2649 - 2750 °F
Solidus	1454 °C	2649 °F
Liquidus	1510 °C	2750 °F

Component Elements Properties	Metric	English	Comments
Carbon, C	0.15 - 0.40 %	0.15 - 0.40 %
Chromium, Cr	12 - 14 %	12 - 14 %
Iron, Fe	86 %	86 %	as balance
Manganese, Mn	<= 1.0 %	<= 1.0 %
Nickel, Ni	<= 0.50 %	<= 0.50 %
Phosphorous, P	<= 0.040 %	<= 0.040 %
Silicon, Si	<= 1.0 %	<= 1.0 %
Sulfur, S	<= 0.030 %	<= 0.030 %

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.0000560 ohm-cm	0.0000560 ohm-cm