ALM PA 620-MF Mineral Fiber Filled Nylon 12 SLS Prototyping Polymer
| Category | Polymer , Rapid Prototyping Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | ALM Advanced Laser Materials |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ALM PA 620-MF Mineral Fiber Filled Nylon 12 SLS Prototyping Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Advanced Laser Materials (ALM).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.460 g/cc | 0.0166 lb/in³ | ASTM D1895 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | Sintered Part; ASTM D792 |
| Particle Size | 55 µm | 55 µm | Average D50; Laser Diffraction |
| 30 - 100 µm | 30 - 100 µm | Range (D10 to D90); Laser Diffraction | |
| Melt Flow | 50 g/10 min @Load 5.00 kg, Temperature 235 °C |
50 g/10 min @Load 11.0 lb, Temperature 455 °F |
3 min.; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | XY direction; ASTM D638 |
| Elongation at Break | 4 % | 4 % | XY direction; ASTM D638 |
| Tensile Modulus | 5.70 GPa | 827 ksi | XY direction; ASTM D638 |
| Flexural Modulus | 4.55 GPa | 660 ksi | XY direction; ASTM D790 |
| Izod Impact, Notched | 37.4 J/cm | 70.1 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 310 J/cm | 581 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 184 °C | 363 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 184 °C | 363 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 179 °C | 354 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 6.7e+15 ohm-cm | 6.7e+15 ohm-cm | 50% RH; 500V; ASTM D257 |
| Surface Resistance | 5.2e+15 ohm | 5.2e+15 ohm | 50% RH; 500V; ASTM D257 |
| Dielectric Constant | 3.14 | 3.14 | 50% RH; 500V; ASTM D150 |
Users viewing this material also viewed the following:
- PolyOne Stat-Tech™ AT-CB2/000 CR Acetal (POM) Copolymer
- Omya OMYACARB® 15 - LU Calcium Carbonate
- Resin Technology Group Fusion 543 Ultra Performance Fusion Cyanoacrylate
- 3M Scotch-Weld™ 3535 B/A Off-white Two-Part Urethane Adhesive 3535 B/A Off-white (discontinued **)
- Plastcom SLOVAMID 6 NG GF 20 HLS PA6, 20% glass fibre, combined stability
- Lucite International Colacryl ® TS1631 Acrylic Solution Resin
- Techmer ES HiFill® PA6 GF60 L BK 60% Glass Filled
- A. Schulman INVISION™ VX-5060UI INVISIONTMSoft Touch Polyolefin Thermoplastic
- Hexcel® HexWeb® HRH-10 - 1/8- 1.8 Aramid Fiber/Phenolic Resin Honeycomb
- Arkema Group Pebax® MV 1074 SP 01 Polyether Block Amide (PEBA)
Copyright © lookpolymers.com All Rights Reserved