A. Schulman ComAlloy Comtuf® 410 Polycarbonate/Polyester Alloy

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer	A. Schulman ComAlloy
Trade Name	COMTUF®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	A. Schulman ComAlloy Comtuf® 410 Polycarbonate/Polyester Alloy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Schulman product line.

Physical Properties	Metric	English	Comments
Density	1.21 g/cc	0.0437 lb/in³
Linear Mold Shrinkage	0.0050 cm/cm	0.0050 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	108	108	ASTM D785
Tensile Strength, Ultimate	52.0 MPa	7540 psi	ASTM D638
Elongation at Break	158 %	158 %	ASTM D638
Flexural Strength	77.0 MPa	11200 psi	ASTM D790
Flexural Modulus	2.00 GPa	290 ksi	ASTM D790
Izod Impact, Notched	6.83 J/cm	12.8 ft-lb/in	ASTM D256
Izod Impact, Unnotched	NB	NB	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	131 °C	268 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	116 °C	241 °F	ASTM D648
Glass Transition Temp, Tg	145 - 150 °C	293 - 302 °F

Processing Properties	Metric	English	Comments
Middle Barrel Temperature	254 - 271 °C	489 - 520 °F