3M Scotchcast™ 2130 Flame-Retardant Compound

Category	Other Engineering Material
Manufacturer	3M
Trade Name	Scotchcast™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotchcast™ 2130 Flame-Retardant Compound.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

3M Scotchcast Flame-Retardant Compound 2130 is a two-part polyurethane resin designed to replace the cable jacket when splicing or repairing mine and portable cables. Its unique formulation makes it particularly suited to withstand the rugged conditions under which mine and portable cables must operate. When used in accordance with the appropriate kit confiation, 2130 Compound conforms to MSHA 30 CFR 18.64. Flame-Retardant 2130 Compound is also used as the insulating material for cable splices operating at up to 1000 volts and designed for 90°C continuous use 130°C overload.Information provided by 3M

Physical Properties	Metric	English	Comments
Density	1.215 g/cc	0.04389 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	83	83	ASTM D2240
Tensile Strength at Break	7.45 MPa	1080 psi	ASTM D412
Elongation at Break	377 %	377 %	ASTM D412

Thermal Properties	Metric	English
Maximum Service Temperature, Air	130 °C	266 °F
Minimum Service Temperature, Air	90.0 °C	194 °F
Glass Transition Temp, Tg	-80.0 °C	-112 °F

Electrical Properties	Metric	English	Comments
Dielectric Constant	5.07 @Frequency 60.0 Hz, Temperature 23.0 °C	5.07 @Frequency 60.0 Hz, Temperature 73.4 °F	ASTM D150
	5.82 @Frequency 60.0 Hz, Temperature 60.0 °C	5.82 @Frequency 60.0 Hz, Temperature 140 °F	ASTM D150
	6.24 @Frequency 60.0 Hz, Temperature 90.0 °C	6.24 @Frequency 60.0 Hz, Temperature 194 °F	ASTM D150
Dielectric Strength	14.6 kV/mm	371 kV/in	ASTM D149

Processing Properties	Metric	English	Comments
Cure Time	960 - 1440 min @Temperature 21.0 °C	16.0 - 24.0 hour @Temperature 69.8 °F	De-Mold Time: 1.5-2 hrs
	1440 - 1800 min @Temperature 10.0 °C	24.0 - 30.0 hour @Temperature 50.0 °F	De-Mold Time: 3.5-4 hrs
	>= 2160 min @Temperature 0.000 °C	>= 36.0 hour @Temperature 32.0 °F	De-Mold Time: 6-8 hrs
Gel Time	17.0 min	17.0 min	3M Method TM-67

Descriptive Properties	Value	Comments
Appearance	Black