3M Scotch-Weld™ EZ250030 Polyurethane Reactive (PUR) Easy 250 Wood Adhesive

Category Polymer , Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ EZ250030 Polyurethane Reactive (PUR) Easy 250 Wood Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Polyurethane Reactive (PUR) Easy 250 Wood Adhesive is 100% solid, warm temperature applied, moisture curing urethanes. This product bonds a wide variety of plastics and wood to themselves and to metal glass. Fast setting adhesives ideal for bonding many plastics including polystyrene and polyacrylic.Information provided by 3M
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
Brookfield Viscosity 13000 cP
13000 cP
Thermosel using spindle #27
Mechanical Properties Metric English Comments
Hardness, Shore D 50
50
Tensile Strength at Break 26.9 MPa
3900 psi
ASTM D638 Die C
Elongation at Break 725 %
725 %
ASTM D638 Die C
Shear Strength 0.931 MPa

@Temperature 23.0 °C
135 psi

@Temperature 73.4 °F
Overlap, ABS, Substrate Failure
2.14 MPa

@Temperature 82.0 °C
310 psi

@Temperature 180 °F
Overlap, PVC
3.72 MPa

@Temperature 82.0 °C
540 psi

@Temperature 180 °F
Overlap, Maple
9.17 MPa

@Temperature 23.0 °C
1330 psi

@Temperature 73.4 °F
Overlap, Polyacrylic, Substrate Failure
10.6 MPa

@Temperature 23.0 °C
1540 psi

@Temperature 73.4 °F
Overlap, Maple
12.45 MPa

@Temperature 23.0 °C
1805 psi

@Temperature 73.4 °F
Overlap, PVC
14.5 MPa

@Temperature 23.0 °C
2100 psi

@Temperature 73.4 °F
Overlap, Polycarbonate
1.03 MPa

@Time 605000 sec
150 psi

@Time 168 hour
Overlap, Maple
2.24 MPa

@Time Error in fixSigDigits: @digits must be between 1 a sec
325 psi

@Time Error in fixSigDigits: @digits must be between 1 a hour
Overlap, PVC
3.10 MPa

@Time Error in fixSigDigits: @digits must be between 1 a sec
450 psi

@Time Error in fixSigDigits: @digits must be between 1 a hour
Overlap, Maple
4.14 MPa

@Time 3600 sec
600 psi

@Time 1.00 hour
Overlap, PVC
7.963 MPa

@Time 259000 sec
1155 psi

@Time 72.0 hour
Overlap, Maple
8.55 MPa

@Time 86400 sec
1240 psi

@Time 24.0 hour
Overlap, Maple
8.929 MPa

@Time 3600 sec
1295 psi

@Time 1.00 hour
Overlap, Maple
12.24 MPa

@Time 259000 sec
1775 psi

@Time 72.0 hour
Overlap, PVC
12.45 MPa

@Time 605000 sec
1805 psi

@Time 168 hour
Overlap, PVC
13.1 MPa

@Time 86400 sec
1900 psi

@Time 24.0 hour
Overlap, PVC
Peel Strength 13.1 kN/m
75.0 pli
180°, Polyacrylic, Cotton duck failed during testing
14.5 kN/m
83.0 pli
180°, ABS, Cotton duck failed during testing
16.7 kN/m
95.0 pli
180°, Polycarbonate, Cotton duck failed during testing
17.5 kN/m
100 pli
180°, PVC, Cotton duck failed during testing
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Processing Properties Metric English Comments
Cure Time 0.500 min
0.00833 hour
Set Time
Descriptive Properties Value Comments
Appearance white/off-white