3M Scotch-Weld™ 183 B/A Tan Epoxy Adhesive

Category	Polymer , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer	3M
Trade Name	Scotch-Weld™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotch-Weld™ 183 B/A Tan Epoxy Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

3M™ Scotch-Weld™ Epoxy Adhesive 1838 B/A is a controlled flow product. This epoxy adhesives are two-part, room temperature curing structural adhesives with high shear strengths and excellent environmental resistance. Excellent for bonding many metals, woods, rubbers and some plastics.Information provided by 3M

Physical Properties	Metric	English	Comments
Viscosity	100000 - 6.00e+6 cP	100000 - 6.00e+6 cP
	100000 - 6.00e+6 cP	100000 - 6.00e+6 cP

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	80 - 85	80 - 85
Elongation at Break	2.0 - 3.0 %	2.0 - 3.0 %
Shear Strength	8.62 MPa	1250 psi	CRS Overlap, 100% RH at 49°C
	19.0 MPa	2750 psi	CRS Overlap, Tap Water at RT
	22.4 MPa	3250 psi	CRS Overlap, White Gas @ RT
	24.8 MPa	3600 psi	CRS Overlap, Hydraulic Oil at RT
	23.4 - 26.2 MPa	3400 - 3800 psi	CRS Overlap
	3.45 MPa @Temperature 82.0 °C	500 psi @Temperature 180 °F	Aluminum Overlap; ASTM D1002
	10.3 MPa @Temperature -55.0 °C	1500 psi @Temperature -67.0 °F	Aluminum Overlap; ASTM D1002
	13.8 MPa @Temperature 24.0 °C	2000 psi @Temperature 75.2 °F	Aluminum Overlap; ASTM D1002
Peel Strength	0.701 kN/m @Temperature -55.0 °C	4.00 pli @Temperature -67.0 °F	Aluminum T-Peel; ASTM D1876
	0.701 kN/m @Temperature 24.0 °C	4.00 pli @Temperature 75.2 °F	Aluminum T-Peel; ASTM D1876
	0.701 kN/m @Temperature 82.0 °C	4.00 pli @Temperature 180 °F	Aluminum T-Peel; ASTM D1876

Descriptive Properties	Value	Comments
Appearance	Tan	Base
	Tan	Accelerator
	Tan