3D Systems Accura® Xtreme Plastic for SLA® Systems

Category	Polymer , Rapid Prototyping Polymer
Manufacturer	3D Systems Corporation
Trade Name	Accura®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3D Systems Accura® Xtreme Plastic for SLA® Systems.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

For use with solid-state stereolithography (SLA®) systemsApplicationsForm, fit and function prototypesDurable AssembliesSnap fit assembliesTough enclosuresConsumer electronic componentsMaster patterns for RTV/Silicone moldingReplace CNC machining of Polypropylene and ABSFeaturesLook and feel of a durable molded plasticOutstanding durability and impact resistanceThermal Resistance over 60° CEasy to use low viscosity formulationFully developed and tested build stylesAll information provided by 3D Systems.

Physical Properties	Metric	English	Comments
Density	1.13 g/cc @Temperature 25.0 °C	0.0408 lb/in³ @Temperature 77.0 °F	Liquid
	1.19 g/cc @Temperature 25.0 °C	0.0430 lb/in³ @Temperature 77.0 °F	Solid
Viscosity	250 - 300 cP @Temperature 30.0 °C	250 - 300 cP @Temperature 86.0 °F

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	86	86
Tensile Strength, Yield	38.0 - 44.0 MPa	5510 - 6380 psi	ASTM D638
Elongation at Break	14 - 22 %	14 - 22 %	ASTM D638
Tensile Modulus	1.79 - 1.98 GPa	260 - 287 ksi	ASTM D638
Flexural Strength	52.0 - 71.0 MPa	7540 - 10300 psi	ASTM D790
Flexural Modulus	1.52 - 2.07 GPa	220 - 300 ksi	ASTM D790
Izod Impact, Notched	0.350 - 0.520 J/cm	0.656 - 0.974 ft-lb/in	ASTM D256
Penetration	4.1	4.1	mils

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	62.0 °C	144 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	54.0 °C	129 °F	ASTM D648
Glass Transition Temp, Tg	52.0 °C	126 °F	DMA, E"

Descriptive Properties	Value	Comments
Appearance	Grey
Critical Exposure (mJ/cm²)	11.7