Polymer Property : Dielectric Strength = 217 kV/mm Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Electrical Properties	Metric	English	Comments
Dielectric Strength	217 kV/mm	5500 kV/in	ASTM D-149
Saint-Gobain NortonÂ® ECTFE Fluoropolymer Film Features/Benefits:Outstanding release propertiesPerformance from -200Â°C (-328Â°F) to 165Â°C (330Â°F)High dielectric strengthExcellent chemical, radiation, weather and abrasion resistanceNon..
Dielectric Strength	217 kV/mm	5500 kV/in	ASTM D-149
Saint-Gobain NortonÂ® ETFE Fluoropolymer Film Features/Benefits:Superior release propertiesExcellent weatherabilityPerformance from -200Â°C (-328Â°F) to 165Â°C (330Â°F)Excellent chemical and mechanical propertiesThermoformableProduct th..
Dielectric Strength	217 kV/mm	5500 kV/in	ASTM D149
Specialty Coating Systems Parylene D Poly (P-Xylylene) Coating Parylene D is a polymer of para-xylylene modified by the substitution of chlorine atoms for two of the aromatic hydrogen atoms. Parylene D is similar in properties to Parylene C with the added abili..
Dielectric Strength	217 kV/mm	5510 kV/in	Flat sheets in air placed between 1/4 in diameter brass electrodes with 0.8 mm (1/32 in) edge radius subjected to 60 cycles AC voltage at 600V/s rate of rise to the breakdown voltage.; ASTM D149-81
DuPont™ Kapton® 200A Polyimide Film, 50 Micron Thickness Film thickness 50 micron 2.0 mil)Kapton® Type A is a lower modulus film, which is conducive to dynamic flex applications.General Kapton® information: Kapton® is synthesized by polymerizing an ar..
Dielectric Strength	217 kV/mm	5510 kV/in	Flat sheets in air placed between 1/4 in diameter brass electrodes with 0.8 mm (1/32 in) edge radius subjected to 60 cycles AC voltage at 600V/s rate of rise to the breakdown voltage.; ASTM D149-81
DuPont™ Kapton® 200FPC Polyimide Film, 50 Micron Thickness Film thickness 50 micron 2.0 mil)All purpose polyimide film. Can be laminated, diecut, slit, formed, or adhesive-coated. Similar to Kapton® Type VN with improved bondability. Available in thickn..
Dielectric Strength	217 kV/mm	5510 kV/in	Flat sheets in air placed between 1/4 in diameter brass electrodes with 0.8 mm (1/32 in) edge radius subjected to 60 cycles AC voltage at 600V/s rate of rise to the breakdown voltage.; ASTM D149-81
DuPont™ Kapton® 200ZT Polyimide Film, 50 Micron Thickness Film thickness 50 micron 2.0 mil)All purpose polyimide film. Can be laminated, diecut, slit, formed, or adhesive-coated. Similar to Kapton® Type VN and HN with superior bondability. Available in..
Dielectric Strength	217 kV/mm	5500 kV/in	Short Time; 1 mil
Parylene Coating Services D Poly (P-Xylylene) Monomer is dichloro para-xylylene. Parylene D is recommended where high temperature resistance is needed; it can be used up to 140°C where oxygen is present.Parylene is a generic name for poly-par..
Dielectric Strength	217 kV/mm	5510 kV/in	Flat sheets in air placed between 1/4 in diameter brass electrodes with 0.8 mm (1/32 in) edge radius subjected to 60 cycles AC voltage at 600V/s rate of rise to the breakdown voltage.; ASTM D149-81
DuPont™ Kapton® 200HN Polyimide Film, 50 Micron Thickness Film thickness 50 micron 2.0 mil)All purpose polyimide film. Can be laminated, diecut, slit, formed, or adhesive-coated. Available in thicknesses from 0.3 mil (7.5 µm) to 5 mil (125 µm).General ..
Dielectric Strength	217 kV/mm	5510 kV/in	Flat sheets in air placed between 1/4 in diameter brass electrodes with 0.8 mm (1/32 in) edge radius subjected to 60 cycles AC voltage at 600V/s rate of rise to the breakdown voltage.; ASTM D149-81
DuPont™ Kapton® 200VN Polyimide Film, 50 Micron Thickness Film thickness 50 micron 2.0 mil)All purpose polyimide film. Can be laminated, diecut, slit, formed, or adhesive-coated. Similar to Kapton® Type HN with added dimensional stability. Available in..