Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.000100 ohm-cm @Temperature 400 °C |
0.000100 ohm-cm @Temperature 752 °F |
|
Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 400 °C |
0.000100 ohm-cm @Temperature 752 °F |
|
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 400 °C |
0.000100 ohm-cm @Temperature 752 °F |
|
Haynes Ultimet® alloy, 12.7-50.8 mm bar Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 400 °C |
0.000100 ohm-cm @Temperature 752 °F |
|
Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 400 °C |
0.000100 ohm-cm @Temperature 752 °F |
|
Haynes Ultimet® alloy, 6.3-38.1 mm plate Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 400 °C |
0.000100 ohm-cm @Temperature 752 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 400 °C |
0.000100 ohm-cm @Temperature 752 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 316°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 400 °C |
0.000100 ohm-cm @Temperature 752 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 427°C (800°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 400 °C |
0.000100 ohm-cm @Temperature 752 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 649°C (1200°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 400 °C |
0.000100 ohm-cm @Temperature 752 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 760°C (1400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 400 °C |
0.000100 ohm-cm @Temperature 752 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 982°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 400 °C |
0.000100 ohm-cm @Temperature 752 °F |
|
Haynes Ultimet® alloy, all-weld metal, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 400 °C |
0.000100 ohm-cm @Temperature 752 °F |
|
Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 400 °C |
0.000100 ohm-cm @Temperature 752 °F |
|
Haynes Ultimet® alloy, all-weld metal, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 400 °C |
0.000100 ohm-cm @Temperature 752 °F |
|
Haynes Ultimet® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 400 °C |
0.000100 ohm-cm @Temperature 752 °F |
|
Haynes Ultimet® alloy, plate, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 400 °C |
0.000100 ohm-cm @Temperature 752 °F |
|
Haynes Ultimet® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 100 °C |
0.000100 ohm-cm @Temperature 212 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Gas Tungsten Arc Welded (GTAW) All Weld Cruciform Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 100 °C |
0.000100 ohm-cm @Temperature 212 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 100 °C |
0.000100 ohm-cm @Temperature 212 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Sheet Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 100 °C |
0.000100 ohm-cm @Temperature 212 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 100 °C |
0.000100 ohm-cm @Temperature 212 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Plate, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 100 °C |
0.000100 ohm-cm @Temperature 212 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Plate, Annealed Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 100 °C |
0.000100 ohm-cm @Temperature 212 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Sheet, Cold-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 100 °C |
0.000100 ohm-cm @Temperature 212 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl.. |
|||
Electrical Resistivity | 0.000100 ohm-cm @Temperature 100 °C |
0.000100 ohm-cm @Temperature 212 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl.. |