Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.000137 ohm-cm @Temperature 500 °C |
0.000137 ohm-cm @Temperature 932 °F |
|
Haynes 625 alloy, 20% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 800 °C |
0.000137 ohm-cm @Temperature 1470 °F |
|
Haynes 625 alloy, 20% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 500 °C |
0.000137 ohm-cm @Temperature 932 °F |
|
Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 800 °C |
0.000137 ohm-cm @Temperature 1470 °F |
|
Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 500 °C |
0.000137 ohm-cm @Temperature 932 °F |
|
Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 800 °C |
0.000137 ohm-cm @Temperature 1470 °F |
|
Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 500 °C |
0.000137 ohm-cm @Temperature 932 °F |
|
Haynes 625 alloy, 40% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 800 °C |
0.000137 ohm-cm @Temperature 1470 °F |
|
Haynes 625 alloy, 50% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 500 °C |
0.000137 ohm-cm @Temperature 932 °F |
|
Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 800 °C |
0.000137 ohm-cm @Temperature 1470 °F |
|
Haynes 625 alloy, cold rolled and 1050°C mill-annealed sheet Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 500 °C |
0.000137 ohm-cm @Temperature 932 °F |
|
Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 500 °C |
0.000137 ohm-cm @Temperature 932 °F |
|
Haynes 625 alloy, plate after 1000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 500 °C |
0.000137 ohm-cm @Temperature 932 °F |
|
Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 800 °C |
0.000137 ohm-cm @Temperature 1470 °F |
|
Haynes 625 alloy, plate after 4000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 800 °C |
0.000137 ohm-cm @Temperature 1470 °F |
|
Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 800 °C |
0.000137 ohm-cm @Temperature 1470 °F |
|
Haynes Hastelloy® B-3® alloy, 0% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 200 °C |
0.000137 ohm-cm @Temperature 392 °F |
|
Haynes Hastelloy® B-3® alloy, 0% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
Electrical Resistivity | 0.000137 ohm-cm | 0.000137 ohm-cm | RT |
Haynes Hastelloy® B-3® alloy, 10% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 100 °C |
0.000137 ohm-cm @Temperature 212 °F |
|
Haynes Hastelloy® B-3® alloy, 10% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 800 °C |
0.000137 ohm-cm @Temperature 1470 °F |
|
Haynes Hastelloy® B-3® alloy, 3.2 mm bright annealed sheet The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 800 °C |
0.000137 ohm-cm @Temperature 1470 °F |
|
Haynes Hastelloy® B-3® alloy, 40% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
Electrical Resistivity | 0.000137 ohm-cm | 0.000137 ohm-cm | RT |
Haynes Hastelloy® B-3® alloy, 50% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
Electrical Resistivity | 0.000137 ohm-cm | 0.000137 ohm-cm | RT |
Haynes Hastelloy® B-3® alloy, 6.3 mm plate The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 100 °C |
0.000137 ohm-cm @Temperature 212 °F |
|
Haynes Hastelloy® B-3® alloy, 6.3 mm plate The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
Electrical Resistivity | 0.000137 ohm-cm | 0.000137 ohm-cm | 3% tolerance on sizes below 0.02, 5% tolerance on sizes above 0.02 |
California Fine Wire Stablohm 825 Nickel Chromium Resistance Wire All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
Electrical Resistivity | 0.000137 ohm-cm | 0.000137 ohm-cm | RT |
Haynes Hastelloy® B-3® alloy, heat treated at 1065°C, rapid quenched The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ea.. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 500 °C |
0.000137 ohm-cm @Temperature 932 °F |
|
Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 800 °C |
0.000137 ohm-cm @Temperature 1470 °F |
|
Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
Electrical Resistivity | 0.000137 ohm-cm @Temperature 800 °C |
0.000137 ohm-cm @Temperature 1470 °F |
|
Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |