Polymer Property : Electrical Resistivity = 0.000135 ohm-cm Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.000135 ohm-cm @Temperature 300 Â°C	0.000135 ohm-cm @Temperature 572 Â°F
Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 1000 Â°C	0.000135 ohm-cm @Temperature 1830 Â°F
Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 1000 Â°C	0.000135 ohm-cm @Temperature 1830 Â°F
Haynes 625 alloy, 10% cold reduction, 1010Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 300 Â°C	0.000135 ohm-cm @Temperature 572 Â°F
Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 300 Â°C	0.000135 ohm-cm @Temperature 572 Â°F
Haynes 625 alloy, 20% cold reduction, 1175Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 1000 Â°C	0.000135 ohm-cm @Temperature 1830 Â°F
Haynes 625 alloy, 30% cold reduction, 1065Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 300 Â°C	0.000135 ohm-cm @Temperature 572 Â°F
Haynes 625 alloy, 30% cold reduction, 1120Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 1000 Â°C	0.000135 ohm-cm @Temperature 1830 Â°F
Haynes 625 alloy, 30% cold reduction, 1120Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 300 Â°C	0.000135 ohm-cm @Temperature 572 Â°F
Haynes 625 alloy, 30% cold reduction, 1175Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 1000 Â°C	0.000135 ohm-cm @Temperature 1830 Â°F
Haynes 625 alloy, 30% cold reduction, 1175Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 1000 Â°C	0.000135 ohm-cm @Temperature 1830 Â°F
Haynes 625 alloy, 40% cold reduction, 1065Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 300 Â°C	0.000135 ohm-cm @Temperature 572 Â°F
Haynes 625 alloy, 40% cold reduction, 1175Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 1000 Â°C	0.000135 ohm-cm @Temperature 1830 Â°F
Haynes 625 alloy, 40% cold reduction, 1175Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 300 Â°C	0.000135 ohm-cm @Temperature 572 Â°F
Haynes 625 alloy, 50% cold reduction, 1065Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 1000 Â°C	0.000135 ohm-cm @Temperature 1830 Â°F
Haynes 625 alloy, 50% cold reduction, 1175Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 300 Â°C	0.000135 ohm-cm @Temperature 572 Â°F
Haynes 625 alloy, cold rolled and 1050Â°C mill-annealed sheet Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 1000 Â°C	0.000135 ohm-cm @Temperature 1830 Â°F
Haynes 625 alloy, cold rolled and 1050Â°C mill-annealed sheet Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 300 Â°C	0.000135 ohm-cm @Temperature 572 Â°F
Haynes 625 alloy, plate after 1000 hours at 650Â°C (1200Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 300 Â°C	0.000135 ohm-cm @Temperature 572 Â°F
Haynes 625 alloy, plate after 1000 hours at 760Â°C (1400Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 1000 Â°C	0.000135 ohm-cm @Temperature 1830 Â°F
Haynes 625 alloy, plate after 1000 hours at 760Â°C (1400Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 300 Â°C	0.000135 ohm-cm @Temperature 572 Â°F
Haynes 625 alloy, plate after 4000 hours at 650Â°C (1200Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Electrical Resistivity	0.000135 ohm-cm	0.000135 ohm-cm	Temperature Factor is 1.06 at 800°C (1470°F). Temperature Factor is 1.07 at 1000°C (1830°F). Temperature Factor is 1.08 at 1200°C (2190°F).
Resistalloy International Fecralloy™ 135 Electrical Resistance Steel Ferritic stainless steel with aluminum. Available as wire, bar, and strip. Used mainly for electrical elements in both industrial and domestic applications. Industrial applications vary from small ..
Electrical Resistivity	0.000135 ohm-cm @Temperature 1000 °C	0.000135 ohm-cm @Temperature 1830 °F
Haynes 625 alloy, 50% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Electrical Resistivity	0.000135 ohm-cm @Temperature 300 °C	0.000135 ohm-cm @Temperature 572 °F
Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Electrical Resistivity	0.000135 ohm-cm @Temperature 1000 °C	0.000135 ohm-cm @Temperature 1830 °F
Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Electrical Resistivity	0.000135 ohm-cm @Temperature 300 °C	0.000135 ohm-cm @Temperature 572 °F
Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var..
Electrical Resistivity	0.000135 ohm-cm @Temperature 1000 °C	0.000135 ohm-cm @Temperature 1830 °F
Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Electrical Resistivity	0.000135 ohm-cm @Temperature 300 °C	0.000135 ohm-cm @Temperature 572 °F
Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..