Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.000128 ohm-cm @Temperature 400 °C |
0.000128 ohm-cm @Temperature 752 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed, 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, gas tungsten arc welded Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, weld metal, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, weld metal, aged at 649°C (1200°F) for 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 400 °C |
0.000128 ohm-cm @Temperature 752 °F |
|
Haynes 242® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 400 °C |
0.000128 ohm-cm @Temperature 752 °F |
|
Haynes 242® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 400 °C |
0.000128 ohm-cm @Temperature 752 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and 40% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 400 °C |
0.000128 ohm-cm @Temperature 752 °F |
|
Haynes 242® alloy, hot rolled plate, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good thermal.. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Electrical Resistivity | 0.000128 ohm-cm @Temperature 25.0 °C |
0.000128 ohm-cm @Temperature 77.0 °F |
specimen aged 16000 hours at 650°C (1200°F) |
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |