Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.0001251 ohm-cm @Temperature 200 °C |
0.0001251 ohm-cm @Temperature 392 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed, 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Electrical Resistivity | 0.0001251 ohm-cm @Temperature 200 °C |
0.0001251 ohm-cm @Temperature 392 °F |
|
Haynes 242® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Electrical Resistivity | 0.0001251 ohm-cm @Temperature 200 °C |
0.0001251 ohm-cm @Temperature 392 °F |
|
Haynes 242® alloy, after 1000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Electrical Resistivity | 0.0001251 ohm-cm @Temperature 200 °C |
0.0001251 ohm-cm @Temperature 392 °F |
|
Haynes 242® alloy, after 4000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Electrical Resistivity | 0.0001251 ohm-cm @Temperature 200 °C |
0.0001251 ohm-cm @Temperature 392 °F |
|
Haynes 242® alloy, after 8000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Electrical Resistivity | 0.0001251 ohm-cm @Temperature 200 °C |
0.0001251 ohm-cm @Temperature 392 °F |
|
Haynes 242® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Electrical Resistivity | 0.0001251 ohm-cm @Temperature 200 °C |
0.0001251 ohm-cm @Temperature 392 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Electrical Resistivity | 0.0001251 ohm-cm @Temperature 200 °C |
0.0001251 ohm-cm @Temperature 392 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Electrical Resistivity | 0.0001251 ohm-cm @Temperature 200 °C |
0.0001251 ohm-cm @Temperature 392 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and 40% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Electrical Resistivity | 0.0001251 ohm-cm @Temperature 200 °C |
0.0001251 ohm-cm @Temperature 392 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Electrical Resistivity | 0.0001251 ohm-cm @Temperature 200 °C |
0.0001251 ohm-cm @Temperature 392 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed, 40% cold work, aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Electrical Resistivity | 0.0001251 ohm-cm @Temperature 200 °C |
0.0001251 ohm-cm @Temperature 392 °F |
|
Haynes 242® alloy, cold rolled sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Electrical Resistivity | 0.0001251 ohm-cm @Temperature 200 °C |
0.0001251 ohm-cm @Temperature 392 °F |
|
Haynes 242® alloy, hot rolled plate, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good thermal.. |