Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 20.0 °C |
0.0000950 ohm-cm @Temperature 68.0 °F |
|
Industeel NUCL 18.10 B4 Natural Boron (Min 1% wt) Alloyed 304 Stainless Steel Description: Isotope B10 has the property to capture neutrons produced by nuclear reactions. Natural boron contains about 19.9 at% or 18.45 wt % of B10 isotope, the remaining being B11 isotope. NUCL.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 20.0 °C |
0.0000950 ohm-cm @Temperature 68.0 °F |
|
Industeel URANUS® B26 6 Mo High Performance Super-Austenitic Stainless Steel with PREN = 43 Description: URANUS® B26 (UR B26) is a 25% Ni, 20% Cr, 6% Mo superaustenitic stainless steel grade with 0.2 % nitrogen additions, particularly designed for high structural stability and high corr.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, cold worked sheet, 20 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, hot rolled and 1230°C solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature sheet after 100 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature sheet after 1000 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature sheet after 1000 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature sheet after 500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature sheet after 500 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Electrical Resistivity | 0.0000950 - 0.000105 ohm-cm | 0.0000950 - 0.000105 ohm-cm | |
AK Steel 18 SR® Ferritic Stainless steel AK Steel 18 SR® provides excellent resistance to high temperature scaling - far superior to that of Type 446 stainless steel. This material is readily welded by conventional methods. It is not su.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 20.0 °C |
0.0000950 ohm-cm @Temperature 68.0 °F |
|
Industeel UREA 25.22.2 Plants Description: CLI UREA 25.22.2 chemical composition has been optimized for specific uses in Urea plants. It is a 310L modified austenitic stainless steel with low carbon, low silicon and high nitroge.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Electrical Resistivity | 0.0000950 ohm-cm @Temperature 1000 °C |
0.0000950 ohm-cm @Temperature 1830 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |