Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 5.00 min | 0.0833 hour | With Primer (Fixture) |
ND Industries StudGrade® 131 Permanent CT Threadlocker General DescriptionHigh strength threadlockers for maximum security. Suitable for most applications where disassembly is not required.Typical Usesstuds and bolts, and threaded pipe fittings.Meets m.. |
|||
Cure Time | 5.00 min | 0.0833 hour | With Primer (Fixture) |
ND Industries StudGrade® 140 Permanent Threadlocker General DescriptionHigh strength threadlockers for maximum security. Suitable for most applications where disassembly is not required.Typical Usesstuds and bolts, and threaded pipe fittings.Meets m.. |
|||
Cure Time | 5.00 - 10.0 min @Temperature 138 °C |
0.0833 - 0.167 hour @Temperature 280 °F |
|
Quantum Composites AMC™ 8590 BK 53% Carbon Fiber Reinforced Vinyl Ester SMC AMC™ 8590 BK is a vinyl ester, chopped carbon fiber reinforced engineered structural composite molding compound. It is easily moldable and provides parts that are high strength, fatigue resistant,.. |
|||
Cure Time | 5.00 - 10.0 min @Temperature 138 °C |
0.0833 - 0.167 hour @Temperature 280 °F |
|
Quantum Composites AMC™ 8593 NT 50% Carbon Fiber Reinforced SMC AMC™ 8593 NT is a chopped carbon fiber reinforced engineered structural composite molding compound. It is easily moldable and provides parts that are high strength, fatigue resistant, with high he.. |
|||
Cure Time | 5.00 - 10.0 min | 0.0833 - 0.167 hour | |
Quantum Composites LYTEX® 4182 50-55% Carbon Fiber Reinforced Epoxy SMC LYTEX 4182 is an epoxy ESC molding compound designed for structural applications requiring excellent mechanical properties, retention of properties at elevated temperatures, good chemical resistance.. |
|||
Cure Time | 5.00 min @Temperature 150 °C |
0.0833 hour @Temperature 302 °F |
|
Reltek BONDiT™ A-43 Bonding Agent, Primer and Adhesive Key Properties: Adhesion promoter for most thermoplastics, thermoset materials, elastomers, polyurethanes.Can be used on metals, glass and ceramicApplications: High functionality produces good bond .. |
|||
Cure Time | 5.00 - 10.0 min | 0.0833 - 0.167 hour | Average value: 7.50 min Grade Count:3 |
Overview of materials for Epoxy/Carbon Fiber Composite This property data is a summary of similar materials in the MatWeb database for the category "Epoxy/Carbon Fiber Composite". Each property range of values reported is minimum and maximum values of a.. |
|||
Cure Time | 5.00 min @Temperature 25.0 °C |
0.0833 hour @Temperature 77.0 °F |
|
Henkel Frekote 915WB Mold Cleaner A water-based cleaner for composite and metal molds. The surfactants and emulsifiers in combination with soft abrasives give excellent cleaning results without dulling or scratching the surface.Bene.. |
|||
Cure Time | 5.00 - 45.0 min | 0.0833 - 0.750 hour | |
Taiwan PU Corporation UR80 Polyester Urethane Rubber UR80 is a polyester urethane rubber which is an easy to process millable gum especially developed for improved compounding and processing benefits. It can be processed and compounded by the use of .. |
|||
Cure Time | 5.00 - 10.0 min | 0.0833 - 0.167 hour | Tack-free time |
Master Bond MasterSil 707FR Flame Retardant Silicone Adhesive Description: MasterSil 707FR is a one component, high performance RTV silicone that is mainly used for its flame retardancy. It is UL listed with a flame classification for 94V-1 for thicknesses of .. |
|||
Cure Time | 5.00 min @Temperature 100 °C |
0.0833 hour @Temperature 212 °F |
|
Tra-Con Tra-Bond F123HV Color Keyed Thixotropic Epoxy Adhesive TRA-BOND F123 HV is a fast cure, high viscosity, two-component epoxy formulation that signals both proper mixing and curing when bonding fiber optic bundles, potting glass fibers, and/or terminating.. |
|||
Cure Time | 5.00 - 20.0 min | 0.0833 - 0.333 hour | for compression molded lab sheets |
TSE Industries Millathane® 28 Millable Polyester Polyurethane Rubber Millathane 28 has excellent resistance to gas (e.g., nitrogen) permeability as well as very good abrasion resistance and low temperature properties. This polyurethane rubber was designed for automot.. |
|||
Cure Time | 5.00 min @Temperature 150 °C |
0.0833 hour @Temperature 302 °F |
|
Loctite® 3563 Epoxy Snap Cure Underfill COB/DCA Encapsulants are essential to the reliability of flip chip assemblies because they minimize the thermal mismatch between the flip chip and substrate.Loctite® Underfills and Encapsulants imp.. |
|||
Cure Time | 5.00 min | 0.0833 hour | |
Loctite® SpeedBonder™ 324 High Impact Acrylic Bonding Adhesive Acrylic Bonding AdhesivesLoctite® Acrylic Adhesives were developed for bonding applications that require tensile, shear and peel strength combined with maximum impact, stress and shock resistance. .. |
|||
Cure Time | 5.00 min | 0.0833 hour | |
Loctite® SpeedBonder™ 325 High Temperature Acrylic Bonding Adhesive Acrylic Bonding AdhesivesLoctite® Acrylic Adhesives were developed for bonding applications that require tensile, shear and peel strength combined with maximum impact, stress and shock resistance. .. |
|||
Cure Time | >= 5.00 min @Temperature 75.0 °C |
>= 0.0833 hour @Temperature 167 °F |
tack free |
ACC EP WQS EPI Engineered Polymers Water Base Quick Set Epoxy EP WQS Water Base Quick Set, “Powered by Reactamine® Technology”, is a two component 60% solids, no VOC, self-leveling modified epoxy. This versatile new generation epoxy displays low blush, fast.. |
|||
Cure Time | <= 5.00 min | <= 0.0833 hour | Fixture Time with Activator |
3M Scotch-Weld™ TL22 Threadlocker Anaerobic Adhesive 3M™ Scotch-Weld™ Threadlocker Anaerobic Adhesives are one-component anaerobic adhesives that cure and seal threaded assemblies that meet a wide range of applications to prevent vibration loosening.. |
|||
Cure Time | <= 5.00 min | <= 0.0833 hour | Fixture Time with Activator |
3M Scotch-Weld™ TL77 Threadlocker Anaerobic Adhesive 3M™ Scotch-Weld™ Threadlocker Anaerobic Adhesives are one-component anaerobic adhesives that cure and seal threaded assemblies that meet a wide range of applications to prevent vibration loosening.. |
|||
Cure Time | <= 5.00 min | <= 0.0833 hour | Fixture Time with Activator |
3M Scotch-Weld™ TL90 Threadlocker Anaerobic Adhesive 3M™ Scotch-Weld™ Threadlocker Anaerobic Adhesives are one-component anaerobic adhesives that cure and seal threaded assemblies that meet a wide range of applications to prevent vibration loosening.. |
|||
Cure Time | 5.00 min @Pressure 0.345 MPa, Temperature 121 °C |
0.0833 hour @Pressure 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle |
Arlon 51986R020 0.020" (0.508 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Side 1: Cured Silicone RubberSubstrate: Style 7628 Fiberglass Side 2: Uncured Silicone Rubber Interleave: Polyethylene Product Use: Flexible heater substrateAppearance: Red colo.. |
|||
Cure Time | 5.00 min @Pressure 0.345 MPa, Temperature 121 °C |
0.0833 hour @Pressure 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle |
Arlon 51986XA015 0.016" (0.406 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Side 1: Cured Silicone RubberSubstrate: Style 7628 Fiberglass Side 2: Uncured Silicone Rubber Interleave: Polyethylene Appearance: Gray silicone gum and rubber on fiberglass clo.. |
|||
Cure Time | 5.00 min @Pressure 0.345 MPa, Temperature 121 °C |
0.0833 hour @Pressure 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle |
Arlon 56986R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Side 1: Cured Silicone Rubber Substrate: 1564 Style Fiberglass Side 2: Uncured Silicone Rubber Interleave: Polyethylene Product Use: Flame Resistant-flexible heater substrateApp.. |
|||
Cure Time | <= 5.00 min | <= 0.0833 hour | Fixture Time with Activator |
3M Scotch-Weld™ TL42 Threadlocker Anaerobic Adhesive 3M™ Scotch-Weld™ Threadlocker Anaerobic Adhesives are one-component anaerobic adhesives that cure and seal threaded assemblies that meet a wide range of applications to prevent vibration loosening.. |
|||
Cure Time | <= 5.00 min | <= 0.0833 hour | Fixture Time with Activator |
3M Scotch-Weld™ TL72 Threadlocker Anaerobic Adhesive 3M™ Scotch-Weld™ Threadlocker Anaerobic Adhesives are one-component anaerobic adhesives that cure and seal threaded assemblies that meet a wide range of applications to prevent vibration loosening.. |
|||
Cure Time | 5.00 - 20.0 min | 0.0833 - 0.333 hour | |
Resinlab® UR1049 MDI Based Rigid Polyurethane Foam System Resinlab™ UR 1049 is a, two component, water blown, 4 lb per cubic foot, MDI based rigid polyurethane foam system. It is designed to cure completely at room temperature. Being of a closed cell stru.. |
|||
Cure Time | 5.00 - 10.0 min @Temperature 138 - 138 °C |
0.0833 - 0.167 hour @Temperature 280 - 280 °F |
Average value: 5.17 min Grade Count:1 |
Overview of materials for Vinyl Ester Sheet Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Vinyl Ester Sheet Molding Compound". Each property range of values reported is minimum and maximum value.. |
|||
Cure Time | 5.00 min | 0.0833 hour | |
Loctite® 648 High Strength/Rapid Cure Retaining Compound RetainersLoctite Corporation, the pioneer of anaerobic adhesives, has applied this technology to create retaining compounds that increase the shear strength of cylindrical, non-threaded assemblies. .. |
|||
Cure Time | 5.00 min | 0.0833 hour | Fixture time @ 20ºC |
Loctite® Output™ 383 Acrylic Adhesive Acrylic Bonding Adhesives and Thermally Conductive BondersLoctite® Acrylic Adhesives were developed for bonding applications that require tensile, shear and peel strength combined with maximum impa.. |