Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 0.500 - 1.17 min | 0.00833 - 0.0194 hour | On Steel (Fixture) |
ND Industries SuperGlue Ethyl 309 Non-running gel for porous surfaces, general purpose |
|||
Cure Time | <= 0.500 min | <= 0.00833 hour | Phenolic, handling time |
Permabond 731 Cyanoacrylate, toughened PERMABOND® 731 is a toughened cyanoacrylate with very good impact and peel strength when compared to a conventional cyanoacrylate. It bonds rapidly at room temperature and its viscosity is stable o.. |
|||
Cure Time | 0.500 - 0.583 min | 0.00833 - 0.00972 hour | Aluminum, handling time |
Permabond 737 Cyanoacrylate, toughened PERMABOND® 737 is a toughened cyanoacrylate with improved impact and peel strength for maximum flexibility. Its increased temperature resistance and dark color make 737 suitable for a wide range of.. |
|||
Cure Time | 0.500 min @Temperature 23.0 °C |
0.00833 hour @Temperature 73.4 °F |
Drying Time |
Permabond POP Polyolefin Primer Permabond® Polyolefin Primer has been developed for surface treatment of polyolefins, PTFE and silicones prior to bonding with Permabond® Cyanoacrylate adhesives. Due to their low surface energy, .. |
|||
Cure Time | <= 0.500 min | <= 0.00833 hour | Handling time |
Permabond TA440 Toughened Acrylic Adhesive PERMABOND TA440 is a two component structural acrylic adhesive suitable for bonding metals, glass, wood, ferrites, ceramics and some rigid plastics. This adhesive may be used in a variety of structu.. |
|||
Cure Time | 0.500 - 0.583 min | 0.00833 - 0.00972 hour | Rubber set time |
Lord Adhesives 5181 High Viscosity, Black, General Purpose Ethyl Cyanoacrylate Adhesive Lord Cyanoacrylate AdhesivesLord® Cyanoacrylate Adhesives were developed for production situations requiring instant bonds and immediate handling strength, particularly when bonding rubber, metal.. |
|||
Cure Time | 0.500 - 0.667 min | 0.00833 - 0.0111 hour | Metal set time |
Lord Adhesives 9900 Normal Setting, High Viscosity, Odorless, Non-Frosting Methyl Cyanoacrylate Adhesive Lord Cyanoacrylate AdhesivesLord® Cyanoacrylate Adhesives were developed for production situations requiring instant bonds and immediate handling strength, particularly when bonding rubber, metal.. |
|||
Cure Time | 0.500 min | 0.00833 hour | |
Loctite® 312 Acrylic Bonding Adhesive Acrylic Bonding AdhesivesLoctite® Acrylic Adhesives were developed for bonding applications that require tensile, shear and peel strength combined with maximum impact, stress and shock resistance. .. |
|||
Cure Time | 0.500 min | 0.00833 hour | |
Loctite® 422 General Purpose Ethyl Cyanoacrylate Bonding Adhesive Cyanoacrylate Bonding AdhesivesLoctite® technology has made the productivity promises of cyanoacrylate adhesives a reality with the industry's widest selection of high-performance, application-.. |
|||
Cure Time | 0.500 min | 0.00833 hour | |
Loctite® 496 General Purpose Methyl Cyanoacrylate Bonding Adhesive Cyanoacrylate Bonding AdhesivesLoctite® technology has made the productivity promises of cyanoacrylate adhesives a reality with the industry's widest selection of high-performance, application-.. |
|||
Cure Time | 0.500 min | 0.00833 hour | Tack-free; 120 mW/cm^2; varies with substrates |
Loctite® FASTGASKET® 5950 Flange Sealant Silicone Gasketing and Gasketing and Wire TackersLoctite® Silicone Gasketing materials include unique products with excellent resistance, formulations for high operating temperatures, and UV-curing.. |
|||
Cure Time | 0.500 min | 0.00833 hour | |
Loctite® Quick Set™ 404 Industrial Adhesive Cyanoacrylate Bonding AdhesivesLoctite® technology has made the productivity promises of cyanoacrylate adhesives a reality with the industry's widest selection of high-performance, application-.. |
|||
Cure Time | 0.500 min | 0.00833 hour | |
Loctite® Super Bonder® 430 Instant Adhesive Cyanoacrylate Bonding AdhesivesLoctite® technology has made the productivity promises of cyanoacrylate adhesives a reality with the industry's widest selection of high-performance, application-.. |
|||
Cure Time | <= 0.500 min | <= 0.00833 hour | Dry Time |
Loctite® Tak Pak® 7452 Accelerator Surface PreparersLoctite offers a complete line of surface preparation products to ensure the maximum performance of Loctite® Adhesives and Sealants.Loctite® Accelerators are used to increase the .. |
|||
Cure Time | 0.500 - 3.50 min | 0.00833 - 0.0583 hour | ts2; ASTM D2084 (mod) |
ExxonMobil Chlorobutyl 1066 Rubber Product Description: Exxon™ Chlorobutyl rubber is a copolymer of isobutylene and isoprene. The product has characteristic specific gravity of 0.93. The product form is white to light amber bales.In.. |
|||
Cure Time | 0.500 - 4.50 min | 0.00833 - 0.0750 hour | ts2; ASTM D2084 |
ExxonMobil Exxon™ 5066 Chlorinated Star-Branched Butyl Exxon Chloromobutyl is a chlorinated copolymer of isobutylene and isoprene.Information provided by ExxonMobil Chemical |
|||
Cure Time | 0.500 - 0.667 min | 0.00833 - 0.0111 hour | Fixture Rate |
Dymax Magnet Bonder™ 2020 Adhesive DYMAX® Magnet Bonder™ Adhesives for Higher Performance and Lower CostDymax 2020 Magnet Bonder™ AdhesiveAcrylic and methacrylic acid-free; bond ferrite to metal, plated metals, E-coat, sealed cans.. |
|||
Cure Time | 0.500 min | 0.00833 hour | Set Time |
3M Scotch-Weld™ TE030 Polyurethane Reactive Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as .. |
|||
Cure Time | 0.500 min | 0.00833 hour | Set Time |
3M Scotch-Weld™ TE031 Polyurethane Reactive Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as .. |
|||
Cure Time | 0.500 - 1.00 min | 0.00833 - 0.0167 hour | |
Bulk Molding Compounds BMC 940 Vinyl Ester Bipolar Plate Material Product Introduction: Bulk Molding Compounds, Inc. is the largest manufacturer of thermoset bulk molding compounds in North America, serving the automotive, appliance, and electrical markets. BMC t.. |
|||
Cure Time | 0.500 - 1.00 min | 0.00833 - 0.0167 hour | Time to Handling Strength |
3M Scotch-Weld™ PR Gel Plastic and Rubber Instant Adhesive 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesive is designed to give exceptional performance on difficult-to-bond plastic and rubber substrates. This adhesive may be bonded to like substrates .. |
|||
Cure Time | 0.500 - 1.00 min | 0.00833 - 0.0167 hour | Time to Handling Strength |
3M Scotch-Weld™ SI Gel Surface Insensitive Instant Adhesive 3M™ Scotch-Weld™ Surface Insensitive Adhesives bond rough, porous, contaminated, and acidic substrates including wood, cardboard, veneer, fabric, cork, and leather. SI Gel (formerly SB09) is a fas.. |
|||
Cure Time | 0.500 min | 0.00833 hour | Set Time |
3M Scotch-Weld™ TE031 Black Polyurethane Reactive Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as .. |
|||
Cure Time | 0.500 - 0.667 min | 0.00833 - 0.0111 hour | Zinc, handling time |
Permabond 943 Cyanoacrylate, low odor PERMABOND 943 is a low odor, non-fogging non-frosting alkoxyethyl cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate ad.. |
|||
Cure Time | 0.500 - 3.50 min | 0.00833 - 0.0583 hour | ts2; ASTM D2084 |
ExxonMobil Exxon™ 1066 Exxon Chloromobutyl is a chlorinated copolymer of isobutylene and isoprene.Information provided by ExxonMobil Chemical |
|||
Cure Time | 0.500 min | 0.00833 hour | Tack-free; 120 mW/cm^2; varies with substrates |
Loctite® FASTGASKET® 5960 Flange Sealant Silicone Gasketing and Gasketing and Wire TackersLoctite® Silicone Gasketing materials include unique products with excellent resistance, formulations for high operating temperatures, and UV-curing.. |
|||
Cure Time | 0.500 min | 0.00833 hour | at 120 mW/cm^2 |
Loctite® FASTGASKET® 5960 Flange Sealant Silicone Gasketing and Gasketing and Wire TackersLoctite® Silicone Gasketing materials include unique products with excellent resistance, formulations for high operating temperatures, and UV-curing.. |
|||
Cure Time | 0.500 - 1.00 min | 0.00833 - 0.0167 hour | Per 1 mm of wall thickness, compression molding |
Hexion Bakelite™ EP 8412 Epoxy Resin, High Arc Resistance, Improved Electrical Properties, Low Shrinkage Epoxy molding compound, inorganically filled, glass fiber reinforced, heat resistant, dimensionally stable, good electrical and mechanical properties, very good chemical resistance, low viscosity, U.. |
|||
Cure Time | 0.500 - 0.667 min | 0.00833 - 0.0111 hour | Zinc, handling time |
Permabond 947 Cyanoacrylate, low odor PERMABOND 947 is a low odor, non-fogging non-frosting alkoxyethyl cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate ad.. |
|||
Cure Time | 0.500 min | 0.00833 hour | |
Loctite® 415 General Purpose Methyl Cyanoacrylate Bonding Adhesive Cyanoacrylate Bonding AdhesivesLoctite® technology has made the productivity promises of cyanoacrylate adhesives a reality with the industry's widest selection of high-performance, application-.. |