Polymer Property : Injection Pressure = 130 MPa Product List

Processing Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Processing Properties	Metric	English	Comments
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi
Plastcom PLASTAMID® 6 GF 20 002 PA6 reinforced with glass fiber PA 6 for injection molding, reinforced with 20% glass fiber, for moldings used in the automotive, electrical, building, engineering and hobby industry - holders of electric hand tools, hobby tools, ..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi
Plastcom PLASTAMID® 6 GF 25 002 PA6 reinforced with glass fiber PA 6 for injection molding, reinforced with 25% glass fiber, for moldings used in the automotive, electrical, building, engineering and hobby industry - holders of electric hand tools, hobby tools, ..
Injection Pressure	68.9 - 130 MPa	10000 - 18900 psi	Average value: 92.2 MPa Grade Count:17
Overview of materials for Nylon 6, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of a..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 CF20 Polyamide 6 20% Carbon Fiber- Antistatic and Electroconductive Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Electroconductive grade based on carbon fiber reinforcement, very high stiffn..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 CFHI Polyamide 6 - Antistatic and Electroconductive Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Electroconductive grade based on carbon fiber reinforcement, very high stiffn..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 GF20 FRV0 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grades, flammability class V0, reinforced with 20% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 GF50 Polyamide 6 - Glass Fiber Reinforced 50% Glass fiber reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 MCS I8 Polyamide 6 - Impact Modified Increased impact resistance grade. Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main propert..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 MCS V0 Polyamide 6 - Flame Retarded, Unreinforced Flame retarded (class V0), bromine and red phosphorus free, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has th..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 MK30 Polyamide 6 - Mineral Reinforced 30% Mineral filled, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High mechani..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 MS Polyamide 6 - Natural Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.For uncolored parts produced by injection molding, contain including and demo..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 Polyamide 6 - Natural Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High mechanical strength, rigidi..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-29 MS Polyamide 6 - Natural Medium-high viscosity extrusion grade for mono or multilayer blown film, including biaxial oriented films, also for production of monofilament; can be used for injection molding and compounding.For ..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	injection speed: 80 - 120 rpm
Beijing Chemical Industry KAIFA® GL3200 ABS Flame-Retardant Grade Good flammabilityInformation provided by Beijing Chemical Industry Research Institute (Group)
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	injection speed: 80 - 120 rpm
Beijing Chemical Industry KAIFA® GL5200 ABS Extrusion Grade Non-toxic, Superior impact strength at low temp., High gloss, Uniform sheet thickness for vacuum moldingInformation provided by Beijing Chemical Industry Research Institute (Group)
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 GF15 Polyamide 6 - Glass Fiber Reinforced 15% Glass fiber reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 GF20 FRV2 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grade, flammability class V2, reinforced with 20% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning...
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 GF25 Polyamide 6 - Glass Fiber Reinforced 25% Glass fiber reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 M Polyamide 6 - Improved Slip Properties Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Low wear and low friction grade, contains molybdenum disulfide, PTFE.Tarnamid..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 MCS 850 Polyamide 6 - Flame Retarded, Unreinforced Glow wire resistance 850°C, bromine and red phosphorus free, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has ..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 MCS HI Polyamide 6 - Impact Modified Very high impact resistance, cold impact grade (to -40°C). Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has t..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 MF30 Polyamide 6 - Mineral Reinforced 30% Mineral filled, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High mechani..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 MHLS Polyamide 6 - Colored Heat and UV light stabilized grade. Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main proper..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 MT30 Polyamide 6 - Mineral Reinforced 30% Mineral filled, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High mechani..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-29 MCS Polyamide 6 - Colored Colored medium-high viscosity grade for injection molding.Tarnamid® has the following main properties:High mechanical strength, rigidity and hardnessHigh impact strengthHigh vibration damping capac..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-30 MS Polyamide 6 - Natural High viscosity extrusion grade for blown and flat films, including biaxial oriented films, also for extrusion of rods, pipes, plates, sheets, low diameter tubes and for injection molding of thick-wa..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	injection speed: 80 - 120 rpm
Beijing Chemical Industry KAIFA® GL1300 ABS General Purpose Grade Excellent impact properties at low temperaturesInformation provided by Beijing Chemical Industry Research Institute (Group)
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 GF10 GB20 Polyamide 6 - Glass Beads Reinforced 10% Glass fiber and 20% glass beads reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following ..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-27 GF25 FRV0 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grades, flammability class V0, reinforced with 25% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning..
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi	80 MPa is recommended
Azoty Tarnow™ Tarnamid® T-30 MHLS Polyamide 6 - Colored High viscosity heat and UV light stabilized grade for injection molding.Tarnamid® has the following main properties:High mechanical strength, rigidity and hardnessHigh impact strengthHigh vibration..