- Polymer Property : Specific Heat Capacity = 0.141 BTU/lb-°F
Polymer Property : Specific Heat Capacity = 0.141 BTU/lb-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged at 649°C (1200°F) for 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 600 °C |
0.141 BTU/lb-°F @Temperature 1110 °F |
|
| Bohler-Uddeholm BÖHLER W403 VMR® Hot Work Tool Steel W403 VMR is a modified hot work alloy with an excellent combination of hot tensile properties and toughness. The balanced properties of this grade are not only due to chemistry modification, but to .. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 600 °C |
0.141 BTU/lb-°F @Temperature 1110 °F |
|
| Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Annealed 1093°C 1 hr Data provided by Carpenter Technology Corporation.Annealing followed by water quench and low stress grinding prior to tensile testing.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting h.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 600 °C |
0.141 BTU/lb-°F @Temperature 1110 °F |
|
| Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Annealed 1093°C 2 hr Data provided by Carpenter Technology Corporation.Annealing followed by water quench and low stress grinding prior to tensile testing.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting h.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 600 °C |
0.141 BTU/lb-°F @Temperature 1110 °F |
|
| Carpenter BioDur™ CCM® Medical Implant Alloy, Annealed Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur Carpenter CCM alloy.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 600 °C |
0.141 BTU/lb-°F @Temperature 1110 °F |
|
| Carpenter BioDur™ CCM® Medical Implant Alloy, Warm Worked Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur Carpenter CCM alloy.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 600 °C |
0.141 BTU/lb-°F @Temperature 1110 °F |
|
| Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Hot Worked Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur CCM Plus alloy is a.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 600 °C |
0.141 BTU/lb-°F @Temperature 1110 °F |
|
| Carpenter BioDur™ CCM® Medical Implant Alloy, Hot Worked Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur Carpenter CCM alloy.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||