Thermal Properties | Metric | English | Comments |
---|---|---|---|
Specific Heat Capacity | 0.586 J/g-°C @Temperature 620 °C |
0.140 BTU/lb-°F @Temperature 1150 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Specific Heat Capacity | 0.586 J/g-°C @Temperature 620 °C |
0.140 BTU/lb-°F @Temperature 1150 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Specific Heat Capacity | 0.586 J/g-°C @Temperature 620 °C |
0.140 BTU/lb-°F @Temperature 1150 °F |
|
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Specific Heat Capacity | 0.586 J/g-°C @Temperature 620 °C |
0.140 BTU/lb-°F @Temperature 1150 °F |
|
Haynes Hastelloy® N, weld metal as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Specific Heat Capacity | 0.586 J/g-°C @Temperature 620 °C |
0.140 BTU/lb-°F @Temperature 1150 °F |
|
Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Specific Heat Capacity | 0.586 J/g-°C @Temperature 600.0 °C |
0.140 BTU/lb-°F @Temperature 1112 °F |
hardened and tempered |
Bohler-Uddeholm UDDEHOLM VANADIS 30 AISI M2 + Co SUPERCLEAN 3 Powder Metallurgical Cold Work Tool Steel Uddeholm Vanadis 30 is a Co high alloyed powder metallurgy high speed steel corresponding to AISI M3:2 + Co. The high compressive strength, 67 HRC, and good abrasive wear resistance makes Uddeholm V.. |
|||
Specific Heat Capacity | 0.586 J/g-°C @Temperature 600.0 °C |
0.140 BTU/lb-°F @Temperature 1112 °F |
hardened and tempered |
Bohler-Uddeholm UDDEHOLM VANADIS 60 Powder Metallurgically Produced Tool Steel Uddeholm Vanadis 60 is a high alloyed powder metallurgical high speed steel suitable for very demanding cold work applications and for cutting tools. The high carbon and alloying content, Co, Mo, W .. |
|||
Specific Heat Capacity | 0.586 J/g-°C @Temperature 600 °C |
0.140 BTU/lb-°F @Temperature 1110 °F |
hardened and tempered condition |
Assab Steels ASP 60 Cold Work Steel ASP 60 is a W-Mo-V-Co alloyed PM high speed steel characterized by:Highest wear resistanceMaximum compressive strengthGood through hardening propertiesGood toughnessGood dimensional stability on hea.. |
|||
Specific Heat Capacity | 0.586 J/g-°C @Temperature 600 °C |
0.140 BTU/lb-°F @Temperature 1110 °F |
hardened and tempered condition |
Assab Steels ASP 30 Cold Work Steel ASP 30 is a W-Mo-v-Co alloyed PM high speed steel characterized by:High wear resistanceHigh compressive strength at high hardnessGood through hardening propertiesGood toughnessGood dimensional stabi.. |
|||
Specific Heat Capacity | 0.586 J/g-°C @Temperature 620 °C |
0.140 BTU/lb-°F @Temperature 1150 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Specific Heat Capacity | 0.586 J/g-°C @Temperature 620 °C |
0.140 BTU/lb-°F @Temperature 1150 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Specific Heat Capacity | 0.586 J/g-°C @Temperature 620 °C |
0.140 BTU/lb-°F @Temperature 1150 °F |
|
Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Specific Heat Capacity | 0.586 J/g-°C @Temperature 620 °C |
0.140 BTU/lb-°F @Temperature 1150 °F |
|
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Specific Heat Capacity | 0.586 J/g-°C @Temperature 620 °C |
0.140 BTU/lb-°F @Temperature 1150 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Specific Heat Capacity | 0.586 J/g-°C @Temperature 620 °C |
0.140 BTU/lb-°F @Temperature 1150 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |