- Polymer Property : Specific Heat Capacity = 0.115 BTU/lb-°F
Polymer Property : Specific Heat Capacity = 0.115 BTU/lb-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.481 J/g-°C @Temperature 450 °C |
0.115 BTU/lb-°F @Temperature 842 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.481 J/g-°C @Temperature 450 °C |
0.115 BTU/lb-°F @Temperature 842 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.481 J/g-°C @Temperature 450 °C |
0.115 BTU/lb-°F @Temperature 842 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.481 J/g-°C @Temperature 450 °C |
0.115 BTU/lb-°F @Temperature 842 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.481 J/g-°C @Temperature 450 °C |
0.115 BTU/lb-°F @Temperature 842 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.481 J/g-°C @Temperature 450 °C |
0.115 BTU/lb-°F @Temperature 842 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.481 J/g-°C @Temperature 450 °C |
0.115 BTU/lb-°F @Temperature 842 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged 1300 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.481 J/g-°C @Temperature 450 °C |
0.115 BTU/lb-°F @Temperature 842 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.481 J/g-°C @Temperature 450 °C |
0.115 BTU/lb-°F @Temperature 842 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.481 J/g-°C @Temperature 450 °C |
0.115 BTU/lb-°F @Temperature 842 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.481 J/g-°C @Temperature 450 °C |
0.115 BTU/lb-°F @Temperature 842 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.481 J/g-°C @Temperature 450 °C |
0.115 BTU/lb-°F @Temperature 842 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged at 649°C (1200°F) for 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.482 J/g-°C @Temperature 200 °C |
0.115 BTU/lb-°F @Temperature 392 °F |
|
| Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.482 J/g-°C @Temperature 200 °C |
0.115 BTU/lb-°F @Temperature 392 °F |
|
| Haynes Ultimet® alloy, 12.7-50.8 mm bar Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.482 J/g-°C @Temperature 200 °C |
0.115 BTU/lb-°F @Temperature 392 °F |
|
| Haynes Ultimet® alloy, 6.3-38.1 mm plate Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.482 J/g-°C @Temperature 200 °C |
0.115 BTU/lb-°F @Temperature 392 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 760°C (1400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.482 J/g-°C @Temperature 200 °C |
0.115 BTU/lb-°F @Temperature 392 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 982°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.482 J/g-°C @Temperature 200 °C |
0.115 BTU/lb-°F @Temperature 392 °F |
|
| Haynes Ultimet® alloy, all-weld metal, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.482 J/g-°C @Temperature 200 °C |
0.115 BTU/lb-°F @Temperature 392 °F |
|
| Haynes Ultimet® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.481 J/g-°C @Temperature 450 °C |
0.115 BTU/lb-°F @Temperature 842 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Specific Heat Capacity | 0.481 J/g-°C @Temperature 450 °C |
0.115 BTU/lb-°F @Temperature 842 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Specific Heat Capacity | 0.481 J/g-°C @Temperature 450 °C |
0.115 BTU/lb-°F @Temperature 842 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||