Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 25.1 W/m-K @Temperature 871 °C |
174 BTU-in/hr-ft²-°F @Temperature 1600 °F |
|
Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Thermal Conductivity | 25.1 W/m-K @Temperature 871 °C |
174 BTU-in/hr-ft²-°F @Temperature 1600 °F |
|
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Thermal Conductivity | 25.1 W/m-K @Temperature 871 °C |
174 BTU-in/hr-ft²-°F @Temperature 1600 °F |
|
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Thermal Conductivity | 25.1 W/m-K @Temperature 871 °C |
174 BTU-in/hr-ft²-°F @Temperature 1600 °F |
|
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1121°C, air cooled, aged 16 hours at 899°C Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Thermal Conductivity | 25.0 W/m-K @Temperature <=200 °C |
174 BTU-in/hr-ft²-°F @Temperature <=392 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1 0 Annealed, Drawn Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. Its machineability is one of the best of all of the corrosion resistant alloys. The very good machineability of.. |
|||
Thermal Conductivity | 25.0 W/m-K @Temperature <=200 °C |
174 BTU-in/hr-ft²-°F @Temperature <=392 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1 0 Annealed, Rolled Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
Thermal Conductivity | 25.0 W/m-K @Temperature <=200 °C |
174 BTU-in/hr-ft²-°F @Temperature <=392 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1 H12 1/2 hard, Drawn Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
Thermal Conductivity | 25.0 W/m-K @Temperature <=200 °C |
174 BTU-in/hr-ft²-°F @Temperature <=392 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1 H12 1/2 hard, Rolled Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
Thermal Conductivity | 25.0 W/m-K @Temperature <=200 °C |
174 BTU-in/hr-ft²-°F @Temperature <=392 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1 H14 4/4 hard, Rolled Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
Thermal Conductivity | 25.0 W/m-K @Temperature <=200 °C |
174 BTU-in/hr-ft²-°F @Temperature <=392 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1C H12 1/2 hard, Rolled Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
Thermal Conductivity | 25.0 W/m-K @Temperature <=200 °C |
174 BTU-in/hr-ft²-°F @Temperature <=392 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1C H13 3/4 hard, Drawn Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
Thermal Conductivity | 25.0 W/m-K @Temperature <=200 °C |
174 BTU-in/hr-ft²-°F @Temperature <=392 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1C H13 3/4 hard, Rolled Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
Thermal Conductivity | 25.0 W/m-K @Temperature <=200 °C |
174 BTU-in/hr-ft²-°F @Temperature <=392 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1 H11 1/4 hard, Rolled Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
Thermal Conductivity | 25.0 W/m-K @Temperature <=200 °C |
174 BTU-in/hr-ft²-°F @Temperature <=392 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1C 0 Annealed, Rolled Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
Thermal Conductivity | 25.0 W/m-K @Temperature <=200 °C |
174 BTU-in/hr-ft²-°F @Temperature <=392 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1C H14 4/4 hard, Rolled Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
Thermal Conductivity | 25.0 W/m-K @Temperature <=200 °C |
174 BTU-in/hr-ft²-°F @Temperature <=392 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1C H15 Spring, Drawn Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
Thermal Conductivity | 25.0 W/m-K @Temperature <=200 °C |
174 BTU-in/hr-ft²-°F @Temperature <=392 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1D H14 4/4 hard, Drawn Copper Alloy, Wire and rod, 2.5< diameter< 5 High Corrosion Resistance: ARCAP alloys are very corrosion resistant to the majority of chemical and physical environments. CLAL can provide data for the corrosion resistance of ARCAP alloys. In par.. |
|||
Thermal Conductivity | 25.0 W/m-K @Temperature 600.0 °C |
174 BTU-in/hr-ft²-°F @Temperature 1112 °F |
hardened and tempered |
Bohler-Uddeholm UDDEHOLM VANADIS 30 AISI M2 + Co SUPERCLEAN 3 Powder Metallurgical Cold Work Tool Steel Uddeholm Vanadis 30 is a Co high alloyed powder metallurgy high speed steel corresponding to AISI M3:2 + Co. The high compressive strength, 67 HRC, and good abrasive wear resistance makes Uddeholm V.. |
|||
Thermal Conductivity | 25.1 W/m-K @Temperature 600.0 °C |
174 BTU-in/hr-ft²-°F @Temperature 1112 °F |
|
AK Steel 13-4 SR® Ferritic Stainless Steel AK Steel 13-4 SR Stainless Steel is a ductile weldable ferritic with 13% Cr and 3.75% Al. The high aluminum content results in a base alloy with high electrical resistivity. It is intended for use w.. |
|||
Thermal Conductivity | 25.0 W/m-K @Temperature 400 °C |
174 BTU-in/hr-ft²-°F @Temperature 752 °F |
hardened and tempered condition |
Assab Steels ASP 60 Cold Work Steel ASP 60 is a W-Mo-V-Co alloyed PM high speed steel characterized by:Highest wear resistanceMaximum compressive strengthGood through hardening propertiesGood toughnessGood dimensional stability on hea.. |
|||
Thermal Conductivity | 25.1 W/m-K @Temperature 871 °C |
174 BTU-in/hr-ft²-°F @Temperature 1600 °F |
|
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include .. |