Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, 12.7-50.8 mm bar Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, 6.3-38.1 mm plate Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 316°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 427°C (800°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 649°C (1200°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 760°C (1400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 982°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, all-weld metal, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, all-weld metal, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, all-weld metal, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, plate, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Ultimet® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |