- Polymer Property : Thermal Conductivity = 149 BTU-in/hr-ft²-°F
Polymer Property : Thermal Conductivity = 149 BTU-in/hr-ft²-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 21.4 W/m-K @Temperature 600 °C |
149 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 263® alloy, cold rolled sheet, solution treated and aged Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle.. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.4 W/m-K @Temperature 700 °C |
149 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes Hastelloy® B-3® alloy, 0% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Thermal Conductivity | 21.4 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® B-3® alloy, 0% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Thermal Conductivity | 21.4 W/m-K @Temperature 700 °C |
149 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes Hastelloy® B-3® alloy, 30% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Thermal Conductivity | 21.4 W/m-K @Temperature 700 °C |
149 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes Hastelloy® B-3® alloy, 40% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Thermal Conductivity | 21.4 W/m-K @Temperature 700 °C |
149 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes Hastelloy® B-3® alloy, 50% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Thermal Conductivity | 21.5 W/m-K | 149 BTU-in/hr-ft²-°F | |
| ATI Wah Chang Zirconium Alloy Zircaloy-4 Zirconium resists corrosive attack in most organic and mineral acids, strong alkalis, and some molten salts. A tightly adherent and protective oxide film protects the metal-oxide interface to provid.. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 50% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 21.4 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® B-3® alloy, heat treated at 1065°C, rapid quenched The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ea.. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||