- Polymer Property : Thermal Conductivity = 10.9 W/m-K
Polymer Property : Thermal Conductivity = 10.9 W/m-K Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 25 alloy, cold worked sheet, 20 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 10.9 W/m-K | 75.6 BTU-in/hr-ft²-°F | RT |
| Haynes HR-160® alloy, plate, aged 1000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Thermal Conductivity | 10.9 W/m-K | 75.6 BTU-in/hr-ft²-°F | RT |
| Haynes HR-160® alloy, plate, aged 8000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 25 alloy, room temperature sheet after 500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, 30% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, 50% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
| Thermal Conductivity | 10.9 W/m-K @Temperature 100 °C |
75.6 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||