- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 500 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 500 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | ASTM D648 |
| Oxford Polymers 30CF 30% Carbon Fiber Reinforced Polyphenylene Sulfide 30% Carbon Fiber Reinforced Polyphenylene SulfideInformation provided by Oxford Polymers. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Average value: 260 °C Grade Count:10 |
| Overview of materials for Diallyl Phthalate (DAP) Molding Compound, Long Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Diallyl Phthalate (DAP) Molding Compound, Long Glass Fiber Filled". Each property range of values report.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | |
| Lehmann & Voss LUVOCOM® 1105-7185 PEEK, with carbon fiber, PTFE, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; low thermal coefficient of expansion.Dynamic stressed parts at high m.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | |
| Lehmann & Voss LUVOCOM® 1105-7760 PEEK, with carbon fiber, PTFE, lubricant modified, high viscosity Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; low thermal coefficient of expansion.Dynamic stressed parts at high m.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 260 °C | >= 500 °F | ASTM D648 |
| IDI Composites E-203 Thermoset Polyester, Sheet ELECTRICAL - U.L. recognized (E53587). Versatile family of compounds designed to meet the most demanding electrical and electronic applications. Excellent dielectric properties and arc/track resista.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | |
| Lehmann & Voss LUVOCOM® 1105-7536 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | |
| Lehmann & Voss LUVOCOM® 1105-7781 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF50 HS L 50% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedInformati.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF50 HS L BK 50% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedAppearanc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Heat Distortion temperature |
| Cosmic Plastics 6230 Long Glass Fiber Filled Iso Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 260 °C | >= 500 °F | |
| Bulk Molding Compounds BMC 102 Glass Filled Thermoset Polyester BMC 102 is a medium strength, glass fiber reinforced molding compound that meets Ford Specification ESF-M3D56-A. It can be supplied in bulk or extruded in pre-weighed slugs and is well suited for in.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 260 °C | >= 500 °F | |
| Bulk Molding Compounds BMC 2270 Mineral Filled, Glass Reinforced Polyester BMC 2270 molding compound is a mineral filled, glass-fiber-reinforced polyester compound suitable for compression and transfer molding. It is a general purpose material with medium impact strength a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 260 °C | >= 500 °F | |
| Bulk Molding Compounds BMC A30-3021 General Purpose Molding Compound BMC A30-3021 is a low shrink, general purpose molding compound formulated for the lighting industry. A30-3021 is temperature stabilized for use in elevated temp. lighting applications. Due to the .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 260 °C | >= 500 °F | |
| Bulk Molding Compounds BMC 1401 Encapsulating Material, Electrical Grade BMC 1401 is an electrical grade of encapsulating material characterized by a balance of soft flow and cure rate to ensure complete and proper encapsulation without voiding. Generally too soft for co.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 260 °C | >= 500 °F | |
| Bulk Molding Compounds BMC 620M Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 620M molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, and stuffer injection molding It is characterized by high impact strength, good mol.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Annealed, 0.125 in bars; ASTM D648 |
| PolyOne Edgetek® SF-35GF-25MN/000 L Polyphenylene Sulfide (PPS), Glass/Mineral Filled
(discontinued **) Description/Features:Glass/Mineral ReinforcedPTFE LubricatedUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 260 °C | >= 500 °F | |
| Bulk Molding Compounds BMC T40-4020-AQ High Strength Arc Quenching Molding Compound BMC T40-4020-AQ was formulated as a high strength arc quenching material for electrical applications. Typical applications are arc hoods and electrical contactors.Information provided by Bulk Moldi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 260 °C | >= 500 °F | |
| Bulk Molding Compounds BMC T60-6006 Wear Resistant Molding Compound BMC T60-6006 is a wear resistant molding compound specifically formulated for applications that require excellent abrasion resistance. Due to its low specific gravity it has substantial cost per cu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 260 °C | >= 500 °F | |
| Bulk Molding Compounds BMC T60-6009 Compression Grade Wear Resistant Molding Compound BMC T60-6009 is a compression grade wear resistant molding compound. This material was specifically formulated for applications that require excellent abrasion resistance. Due to its low specific .. |
|||