Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | ASTM D648 |
Polymer Resources TP-G30 Polybutylene Terephthalate, 30% Glass Reinforced Polybutylene Terephthalate, 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information prov.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | ASTM D648 |
Polymer Resources TPSF-FRG30 Polybutylene Terephthalate, Structural Foam, 30% Glass Reinforced, Flame Retardant Polybutylene Terephthalate, Structural Foam, 30% Glass Reinforced, Flame RetardantProcess: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | ASTM D648 |
Polymer Resources TPSF-G30 Polybutylene Terephthalate, Structural Foam, 30% Glass Reinforced Polybutylene Terephthalate, Structural Foam, 30% Glass Reinforced Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inf.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | 0.125 in; ASTM D 648 |
Matrixx Group 84S7301 Flame Retardant 30% Glass Reinforced PET (V0)
(discontinued **) Data provided by The Matrixx Group, formerly RePlas. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | Unannealed; ASTM D648 |
Techmer ES Electrablend® PEI 04001 MB Stainless Steel Fiber Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Stainless Steel FiberFeatures: Electromagnetic Shielding (EMI)Information provided by TP Composites, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | Unannealed; ASTM D648 |
Techmer ES HiFill FR® PBT GF30 FR 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightFeatures: Flame RetardantUL File Number: E157318Information provided by TP Composites, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® PA6 GF/M40 HS L 40% Glass/Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral, 40% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and LubricatedTPCI# 7395102Informat.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® PA6 GF/M40 HS L BK 40% Glass/Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral, 40% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and LubricatedAppearance: BlackProc.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® PA6 GF/M40 IG BK 40% Glass/Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral, 40% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and LubricatedProcessing Method: In.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® PA6 GF/M40 L 40% Glass/Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral, 40% Filler by WeightAdditive: LubricantFeatures: LubricatedProcessing Method: Injection MoldingInformation provided by T.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® PA6 GF/M55 L BK 15/40% Glass/Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by Weight and Mineral, 40% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® PA6/6 GF/M35 HS BK 35% Glass/Mineral Fiber Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 35% Filler by Weight and Mineral Filler, 35% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | ASTM D648 |
Chase Plastics CP Pryme® N120GL (DAM) Nylon 6, 20% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | ASTM D648 |
Chase Plastics CP Pryme® N140MGHSL (DAM) Nylon 6, 40% Mineral/Glass Reinforced, Heat Stabilized, Internally Lubricated Information provided by Chase Plastics. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | Unannealed; ASTM D648 |
Chase Plastics CP Pryme® N310L (Dry) Nylon 6, 10% Glass Fiber Reinforced, Lubricated, Recycled Content Features: LubricatedRecycled contentForm: PelletsInformation provided by Chase Plastics. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | ASTM D648 |
Chase Plastics CP Pryme® N320GL (DAM) Nylon 6 (Utility Grade), 20% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | ASTM D648 |
Chase Plastics CP Pryme® N340MGL (DAM) Nylon 6 (Utility Grade), 40% Mineral/Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | Unannealed, 0.125 in bars; ASTM D648 |
PolyOne Lubri-Tech™ ES-000/15T Polyethersulfone, PTFE Lubricated
(discontinued **) Description/Features:PTFE LubricatedInformation provided by PolyOne Corporation. |