- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 290 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 290 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | >= 290 °C | >= 554 °F | |
| Lehmann & Voss LUVOCOM® 19-7278 Polyamide 46, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia comp.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 290 °C | >= 554 °F | |
| Lehmann & Voss LUVOCOM® 19-7319 Polyamide 46, with carbon fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Electrically conductive.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 290 °C | >= 554 °F | |
| Lehmann & Voss LUVOCOM® 19-8365 Polyamide 46, with carbon fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia comp.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 290 °C | >= 554 °F | |
| Lehmann & Voss LUVOCOM® 46/CF/15 Polyamide 46, with carbon fiber, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Electrically conductive.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ASTM D648 |
| Kuraray Genestarâ„¢ G1302 Nylon, 30% Glass Filled Abrasion Resistance HB grade. Halogen free, following the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm. It delivers low.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ASTM D648 |
| Kuraray Genestarâ„¢ G1350H Nylon, 35% Glass Filled Standard HB grade. Halogen free, following the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm. It is suitable for use in .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ASTM D648 |
| Mitsui Arlen™ A315 15% Glass Fiber-Reinforced Modified Nylon 6T (COND) ARLEN™ is a heat resistant, modified polyamide 6T developed by Mitsui Chemicals, Inc. With a high melting point (320°C) and a rigidity level comparable to super engineering plastics, it poss.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C @Thickness 3.20 mm |
554 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP LX91475 PEEK (Asia Pacific) LNP* LUBRICOMP* LX91475 is a compound based on Polyetheretherketone resin containing Bearing Grade. Added features of this material include: Easy Molding. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | Unannealed; Flatwise; ISO 75-2/A |
| Solvay Specialty Polymers Amodel® A-8930 HS Polyphthalamide (PPA), 30% Glass Fiber Amodel® A-8930 HS is a 30% glass-fiber-reinforced, heat-stabilized polyphthalamide (PPA) with a high heat deflection temperature and very high tensile strength. Excellent creep resistance and low.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | Unannealed; Flatwise; ISO 75-2/A |
| Solvay Specialty Polymers Amodel® AS-1935 HS Polyphthalamide (PPA), 35% Glass Fiber Amodel® AS-1935 HS is a 35% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material e.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® PA4/6 GF30 FR HS X 30% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat Stabilizer Features: Flame Retardant and Heat StabilizedUL File Number: E.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C @Thickness 3.20 mm |
554 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP LCF62E PEEK LNP* THERMOCOMP* LCF62E is a compound based on Polyetheretherketone resin containing 10% Carbon, 30% Glass Fiber fillers. Added features of this material includes: Easy Molding, Electrically Condu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® PA4/6 GF15 FR HS L 15% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Flame Retardant, Lubricated and Heat St.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C @Thickness 6.40 mm |
554 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® TK-6036H PPA, Glass Filled Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 |
| DSM Stanyl® TE250F3 (DAM) Nylon 46 15% Glass Reinforced, Heat Stabilized, Flame Retardant (North America) Information provided by DSM Engineering Plastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 |
| DSM Stanyl® TE250F6 (DAM) Nylon 46 30% Glass Reinforced, Heat Stabilized, Flame Retardant (North America) Information provided by DSM Engineering Plastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 |
| DSM Stanyl® TE250F9 Nylon 46-45% Glass Reinforced (European and Asian Grade) (Dry) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 |
| DSM Stanyl® TS250F6D Nylon 46-30% Glass Reinforced (Asian Grade) (Dry) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 |
| DSM Stanyl® TW200F8 (DAM) Nylon 46 40% Glass Reinforced, Heat Stabilized (North America) Information provided by DSM Engineering Plastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 |
| DSM Stanyl® TW241F10 (DAM) Nylon 46 50% Glass Reinforced, Heat Stabilized (North America) Information provided by DSM Engineering Plastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 |
| DSM Stanyl® TW241F10 Nylon 46-50% Glass Reinforced (European Grade) (Dry) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 |
| DSM Stanyl® TW241F12 Nylon 46-60% Glass Reinforced (European and Asian Grade) (Dry) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 |
| DSM Stanyl® TW241F6 Nylon 46-30% Glass Reinforced, Heat Stabilized, Lubricated (Asian Grade) (Dry) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 |
| DSM Stanyl® TW271F6 Nylon 46-30% Glass Reinforced (European and Asian Grade) (Dry) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75 |
| Eurotec® Tecomid® NT40 CR30 BK111 HS PPA, 30% carbon fiber reinforced, heat stabilized, natural Information provided by Eurotec® |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® HT1V-6 FWA black 9225 PA6T/6I-GF60 Product description: Grivory HT1V-6 FWA black 9225 is a 60 wt.- % glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | HDT/A; ISO 75-1/2 |
| Akro-Plastic Akromid® T6 GF 50 (3106) PPA Dry, 50% Glass Filled The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ASTM D648 |
| E-Polymers SEPAZ® V330FR 30% Glass Fiber Reinforced Flame Retardant PPA Polyphthal Amide Resin (High Temperature Nylon): SEPAZ PPA is a unique semi-crystalline engineering plastic that bridges the cost-performance gap between traditional engineering thermoplastics and s.. |
|||