- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 360 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 360 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Nylene® 401, Nylon 6 Injection molding grade. Dry As Molded. Nylene 401 is recommended for general purpose nylon molding applications in both thin and heavy sections. Nylene 401 has high flow characteristics at minima.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Nylene® 401, Nylon 6, at 50% Relative Humidity Injection molding grade. Nylene 401 is recommended for general purpose nylon molding applications in both thin and heavy sections. Nylene 401 has high flow characteristics at minimal processing temp.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Nylene® 406 Nylon 6 Injection molding grade. Dry as molded. Nylene 406 is a general purpose, fast cycling molding resin. Crystallization initiators provide fast molding cycles through rapid melt set-up. Parts molded f.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Nylene® 406F Nylon 6 Dry as molded. Injection molding grade. Nylene 406F is a resin formulated to comply with FDA regulation 21 CFR 177.1500 for food contact applications. Nylene 406F is a general purpose, fast cycling.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Nylene® 409 Nylon 6 Dry as molded. Injection molding grade. Nylene 409 is a heat stabilized version of 406 which is a general purpose, fast cycling molding resin. Crystallization initiators provide fast molding cycles.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Nylene® 409 Nylon 6, 50% RH Injection molding grade. Nylene 409 is a heat stabilized version of 406 which is a general purpose, fast cycling molding resin. Crystallization initiators provide fast molding cycles through rapid m.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C @Thickness 3.20 mm |
360 °F @Thickness 0.126 in |
ASTM D648 |
| Ovation Polymers RIGITRON 20415 GF PBT, 15% Glass Reinforced PBT - Glass reinforced (15 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared acco.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ISO 75, ASTM D648 |
| Nilit Nilitop BT N Unfilled, Nucleated PBT Description: Nilitop BT N is an unfilled, nucleated PBT that has excellent cycle times.Key characteristics: Good overall mechanical performanceLow moisture absorptionExcellent UV resistanceExcellent.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | Average value: 182 °C Grade Count:7 |
| Overview of materials for Polysulfone, 10% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are incl.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C @Thickness 3.20 mm |
360 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP HFG25Z PA 11 LNP* Lubricomp* HFG25Z is a compound based on Nylon 11 resin containing 25% Glass Fiber, 10% Graphite. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Solvay TECHNYL® eXten D247 F Nylon 66 & 610 Description: Polyamid 66 & 610, impact modified, alkali resistance, mold release, for injection molding. This material is available in natural color and in colors on requestAvailable in: Asia Pacifi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C @Thickness 3.20 mm |
360 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP WL002 PBT LNP* LUBRICOMP WL002 is a compound based on PBT resin containing 10% PTFE. Added feature of this grade is: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Ultem ATX152R PEI+PCE (Asia Pacific) 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Plastics Group Polifil® 930L Nylon 6 (DAM) Polifil® NYLON 6 provides superior strength and rigidity with electrical resistance and surface lubricity.Applications: AutomotiveHousingsBearingsAppliances Standard processing techniques are appli.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Chase Plastics CP Pryme® N200L (COND, 50% RH) Nylon 6, Internally Lubricated Information provided by Chase Plastics. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ISO-R 75 Method B |
| Hippe PEEK Polyetheretherketone PEEK is a crystalline, easily machinable thermoplastic which is characterized by high tensile and constant good electrical properties between 0°-220°C, as well as due to favorable tribological beh.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Adell BS-30 Nylon 6, General Purpose Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Ashley Polymers Ashlene® 829L Nylon 6 Basic Nylon 6, low viscosity, lubricated.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Ashley Polymers Ashlene® 830LB Nylon 6 Basic Nylon 6, medium viscosity, lubricated black.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Ashley Polymers Ashlene® 835 Nylon 6 Basic Nylon 6 high viscosity, for coating and laminating applications, FDA approved.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Aaron Industries AAROPRENE® AEN 6000-1 Nylon 6 Engineered Resin |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Ashley Polymers Ashlene® 830LW Nylon 6 Basic Nylon 6, medium viscosity, lubricated for general purpose injection molding.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Quantum PEEK Information provided by Quantum Advanced Engineering Plastics |
|||