Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 100 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	38.0 - 41.0 °C	100 - 106 °F	ASTM D648-06
Proto3000 Objet Digital Materials™ DM_8430 Polypropylene-like Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide..
Deflection Temperature at 0.46 MPa (66 psi)	38.0 - 41.0 °C	100 - 106 °F	ASTM D648-06
Proto3000 Objet Digital Materials™ DM_8530_Gray60 Polypropylene-like Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr..
Deflection Temperature at 0.46 MPa (66 psi)	38.0 °C	100 °F	injection molded specimen; ASTM D648
Phillips Sumika Marlex® CHP-010 Thermoplastic Polyolefin (discontinued **) Applications: Soft interior trimSoft touch overmoldingInformation provided by Chevron Phillips.Phillips Sumika Polypropylene Company has been shut down, as announced in 2011.
Deflection Temperature at 0.46 MPa (66 psi)	38.0 °C @Thickness 3.17 mm	100 °F @Thickness 0.125 in	ISO 75
A. Schulman FORMION™ FI 120 Non-Reinforced, Injection Molding Grade Zinc Ionomer DescriptionFormion® FI 120 is a non-reinforced, transparent, injection molding grade Zinc Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and lo..
Deflection Temperature at 0.46 MPa (66 psi)	38.0 °C @Thickness 3.20 mm	100 °F @Thickness 0.126 in	ISO 75
A. Schulman FORMION™ FI 301 Ionomer Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi)	38.0 °C @Thickness 3.20 mm	100 °F @Thickness 0.126 in	ISO 75
A. Schulman FORMION™ FI 301 Ionomer Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi)	38.0 °C @Thickness 3.17 mm	100 °F @Thickness 0.125 in	ISO 75
A. Schulman FORMION™ FI 120 Non-Reinforced, Injection Molding Grade Zinc Ionomer DescriptionFormion® FI 120 is a non-reinforced, transparent, injection molding grade Zinc Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and lo..
Deflection Temperature at 0.46 MPa (66 psi)	38.0 °C @Thickness 3.17 mm	100 °F @Thickness 0.125 in	ISO 75
A. Schulman FORMION™ FI 120 Non-Reinforced, Injection Molding Grade Zinc Ionomer DescriptionFormion® FI 120 is a non-reinforced, transparent, injection molding grade Zinc Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and lo..
Deflection Temperature at 0.46 MPa (66 psi)	38.0 °C @Thickness 3.20 mm	100 °F @Thickness 0.126 in	ISO 75
A. Schulman FORMION™ FI 301 Ionomer Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi)	38.0 °C @Thickness 3.17 mm	100 °F @Thickness 0.125 in	ISO 75
A. Schulman FORMION™ FI 120 Non-Reinforced, Injection Molding Grade Zinc Ionomer DescriptionFormion® FI 120 is a non-reinforced, transparent, injection molding grade Zinc Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and lo..
Deflection Temperature at 0.46 MPa (66 psi)	38.0 °C @Thickness 3.20 mm	100 °F @Thickness 0.126 in	ISO 75
A. Schulman FORMION™ FI 301 Ionomer Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi)	38.0 °C @Thickness 3.17 mm	100 °F @Thickness 0.125 in	ISO 75
A. Schulman FORMION™ FI 120 Non-Reinforced, Injection Molding Grade Zinc Ionomer DescriptionFormion® FI 120 is a non-reinforced, transparent, injection molding grade Zinc Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and lo..
Deflection Temperature at 0.46 MPa (66 psi)	38.0 °C @Thickness 3.20 mm	100 °F @Thickness 0.126 in	ISO 75
A. Schulman FORMION™ FI 301 Ionomer Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi)	38.0 °C @Thickness 3.20 mm	100 °F @Thickness 0.126 in	ISO 75
A. Schulman FORMION™ FI 301 Ionomer Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi)	38.0 °C @Thickness 3.17 mm	100 °F @Thickness 0.125 in	ISO 75
A. Schulman FORMION™ FI 120 Non-Reinforced, Injection Molding Grade Zinc Ionomer DescriptionFormion® FI 120 is a non-reinforced, transparent, injection molding grade Zinc Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and lo..