- Polymer Property : CTE, linear = 9.72 µin/in-°F
Polymer Property : CTE, linear = 9.72 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 17.5 µm/m-°C @Temperature 400 °C |
9.72 µin/in-°F @Temperature 752 °F |
|
| Outokumpu 4306 Cr-Ni Austenitic Stainless Steel General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 400 °C |
9.72 µin/in-°F @Temperature 752 °F |
|
| Outokumpu 4429 Cr-Ni-Mo Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), cold rolled strip/sheet and rod forms. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 400 °C |
9.72 µin/in-°F @Temperature 752 °F |
|
| Outokumpu 4435 Cr-Ni-Mo Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 400 °C |
9.72 µin/in-°F @Temperature 752 °F |
|
| Outokumpu 4436 Cr-Ni-Mo Austenitic Stainless Steel General purpose steel with excellent corrosion resistance, particularly in the presence of halides.Applications: FiltersBraiding for hydraulic hosesShaftsFastenersMarine componentsAvailable in hot r.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 200 °C |
9.72 µin/in-°F @Temperature 392 °F |
|
| Outokumpu 4571 Cr-Ni-Mo Austenitic Stainless Steel Very good corrosion resistance, weldable, and resistant to sensitization.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar,.. |
|||
| CTE, linear | 17.5 - 18.5 µm/m-°C @Temperature 20.0 - 200 °C |
9.72 - 10.3 µin/in-°F @Temperature 68.0 - 392 °F |
|
| PEAK Werkstoff DISPAL S260 Aluminum Alloy, AlSi25Cu4Mg, Condition F Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
| CTE, linear | 17.5 - 18.5 µm/m-°C @Temperature 20.0 - 200 °C |
9.72 - 10.3 µin/in-°F @Temperature 68.0 - 392 °F |
|
| PEAK Werkstoff DISPAL S260 Aluminum Alloy, AlSi25Cu4Mg, Condition T7 Heat Treatment Condition T7 (Quenching in water at RT)Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allo.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 23.0 - 800 °C |
9.72 µin/in-°F @Temperature 73.4 - 1470 °F |
|
| Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 23.0 - 800 °C |
9.72 µin/in-°F @Temperature 73.4 - 1470 °F |
|
| Haynes Multimet® alloy, 12.7 mm (1/2 in.) thick plate, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 23.0 - 800 °C |
9.72 µin/in-°F @Temperature 73.4 - 1470 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 1185°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 23.0 - 800 °C |
9.72 µin/in-°F @Temperature 73.4 - 1470 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 40% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 23.0 - 800 °C |
9.72 µin/in-°F @Temperature 73.4 - 1470 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 10% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 23.0 - 800 °C |
9.72 µin/in-°F @Temperature 73.4 - 1470 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 20% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 20.0 - 500 °C |
9.72 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Industeel UREA 316L Modified 316L Mod Low Si, High Mo Stainless Steel for Urea Plants Description: UREA 316L Modified grade has been specially developed for Urea plant applications. It is a 316L modified stainless steel with extra-low silicon content and substantial higher molybdenum.. |
|||