- Polymer Property : CTE, linear = 8.89 µin/in-°F
Polymer Property : CTE, linear = 8.89 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.0 µm/m-°C @Temperature -55.0 - 288 °C |
8.89 µin/in-°F @Temperature -67.0 - 550 °F |
Y-Direction; IPC-TM-650 2.4.41 |
| Rogers Corporation RO4350B Glass-Reinforced Hydrocarbon and Ceramic Laminate with Thin Film Resistor Foil RO4000® Series High Frequency Circuit Materials are glass-reinforced hydrocarbon and ceramic (not PTFE) laminates with TICER™ TCR® Thin Film Resistor Foils. These laminates are designed for perf.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature -55.0 - 288 °C |
8.89 µin/in-°F @Temperature -67.0 - 550 °F |
Y-Direction; ASTM D3386-94 |
| Rogers Corporation RO4535 Ceramic-Filled, Glass-Reinforced Hydrocarbon Laminate The RO4500™ Series Cost Performance Antenna Grade Laminates are ceramic-filled, glass-reinforced hydrocarbon based materials that provides the controlled dielectric constant, low loss performance a.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 100 °C |
8.89 µin/in-°F @Temperature 212 °F |
|
| Outokumpu 4429 Cr-Ni-Mo Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), cold rolled strip/sheet and rod forms. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature -50.0 - 50.0 °C |
8.89 µin/in-°F @Temperature -58.0 - 122 °F |
Axial; ASTM E831 |
| Chevron Phillips Ryton® BR42C Polyphenylene Sulfide Compound
(discontinued **) Black Polyphenylene Sulfide CompoundRyton® BR42C is a 40% fiberglass reinforced polyphenylene sulfide compound specially formulated to have a low coefficient of friction for use in low surface fric.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 100 °C |
8.89 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Industeel CLC 17.13.3 LN Nitrogen Containing 18Cr-10Ni-2Mo Austenitic Stainless Steel Description: CLC 17-13-3LN is a nitrogen alloyed austenitic stainless steel with Mo additions. Its low carbon content avoids intergranular corrosion, even on welded pieces without an ulterior water .. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 100 °C |
8.89 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Industeel CLC 17.13.5 LN Modified 317LN Mo 4% Austenitic Stainless Steel Description: CLC 17-13-5LN (317LNM) is a Nitrogen alloyed austenitic stainless steel with a high Molybdenum addition (=4%). Alloy CLC 17-13-5LN (317LNM) exhibits austenitic microstructure free of de.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 1093 °C |
8.89 µin/in-°F @Temperature 68.0 - 1999 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged 1300 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 1093 °C |
8.89 µin/in-°F @Temperature 68.0 - 1999 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 23.0 - 500 °C |
8.89 µin/in-°F @Temperature 73.4 - 932 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 5% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 23.0 - 500 °C |
8.89 µin/in-°F @Temperature 73.4 - 932 °F |
|
| Haynes Multimet® alloy, SMAW, 12.7 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 25.0 - 800 °C |
8.89 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 25.0 - 800 °C |
8.89 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 25.0 - 800 °C |
8.89 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 25.0 - 800 °C |
8.89 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 25.0 - 800 °C |
8.89 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 30.0 - 760 °C |
8.89 µin/in-°F @Temperature 86.0 - 1400 °F |
|
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GMAW spray weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 30.0 - 649 °C |
8.89 µin/in-°F @Temperature 86.0 - 1200 °F |
|
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld 3.2 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 23.0 - 500 °C |
8.89 µin/in-°F @Temperature 73.4 - 932 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 35% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 23.0 - 500 °C |
8.89 µin/in-°F @Temperature 73.4 - 932 °F |
|
| Haynes Multimet® alloy, SMAW, 9.5 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 0.000 - 300 °C |
8.89 µin/in-°F @Temperature 32.0 - 572 °F |
|
| CLAL-MSX ARCAP Anticorrosion AP1C H12 1/2 hard, Rolled Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 0.000 - 300 °C |
8.89 µin/in-°F @Temperature 32.0 - 572 °F |
|
| CLAL-MSX ARCAP Anticorrosion AP1 H14 4/4 hard, Drawn Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 0.000 - 300 °C |
8.89 µin/in-°F @Temperature 32.0 - 572 °F |
|
| CLAL-MSX ARCAP Anticorrosion AP1C H15 Spring, Drawn Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature <=427 °C |
8.89 µin/in-°F @Temperature <=801 °F |
|
| AK Steel 17-7 PH® Precipitation Hardening Stainless Steel, Condition A AK Steel 17-7 PH® provides high strength and hardness, excellent fatigue properties, good corrosion resistance, good formability, and minimum distortion upon heat treatment. This alloy provides va.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 25.0 - 800 °C |
8.89 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 30.0 - 649 °C |
8.89 µin/in-°F @Temperature 86.0 - 1200 °F |
|
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW short arc weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 1093 °C |
8.89 µin/in-°F @Temperature 68.0 - 1999 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 100 °C |
8.89 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Industeel CLC 18.9 L General Purpose 18Cr-9Ni Austenitic Stainless Steel Description: CLC 18-9L is a 18Cr-9Ni austenitic stainless steel. The grade contains small amount of ferrite (~ 3%) after solution annealing (1000-1100°C – 1832-2012°F) and water quenching. This k.. |
|||
| CTE, linear | 16.0 µm/m-°C @Temperature 30.0 - 649 °C |
8.89 µin/in-°F @Temperature 86.0 - 1200 °F |
|
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||