Polymer Property : CTE, linear = 8.39 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
| Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
| Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 982°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature sheet after 100 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 0% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 30% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, hot rolled, solution annealed plate, 6.4-12.7 mm (1/2 in.) thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 200 °C |
8.39 µin/in-°F @Temperature 392 °F |
|
| Special Metals INCOLOY® alloy 864 INCOLOY® alloy 8684 (UNS S35135) was specifically developed for automotive exhaust system flexible couplings, EGR tubes, manifolds and tailpipes. It exhibits excellent fatigue resistance, therma.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature after 0% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 21.0 - 538 °C |
8.39 µin/in-°F @Temperature 69.8 - 1000 °F |
|
| Kennametal Stellite Stellite® 31 PM after P/M processing, aged 8 hours at 802°C air cooled Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||