Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 15.08 µm/m-°C @Temperature 24.0 - 300 °C |
8.378 µin/in-°F @Temperature 75.2 - 572 °F |
Mean |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 2 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness Tensile strength (ultimate and yield), shear strength, and elongation values reported here are typical for Cold Rolled Sheet, 2 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness samples. Density a.. |
|||
CTE, linear | 15.08 µm/m-°C @Temperature 24.0 - 300 °C |
8.378 µin/in-°F @Temperature 75.2 - 572 °F |
Mean |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 3 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness Tensile strength (ultimate and yield), shear strength, and elongation values reported here are typical for Cold Rolled Sheet, 3 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness samples. Density a.. |
|||
CTE, linear | 15.08 µm/m-°C @Temperature 24.0 - 300 °C |
8.378 µin/in-°F @Temperature 75.2 - 572 °F |
Mean |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 3 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness Tensile and bearing strengths (ultimate and yield) and elongation values reported here are typical for Cold Rolled Sheet, 3 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness samples. Density and m.. |
|||
CTE, linear | 15.08 µm/m-°C @Temperature 24.0 - 300 °C |
8.378 µin/in-°F @Temperature 75.2 - 572 °F |
Mean |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, Solution Treated Tensile strength (ultimate and yield), and elongation values reported here are typical for Cold Rolled Sheet, Solution Treated samples. Density and magnetic permeability are typical of annealed INCO.. |
|||
CTE, linear | 15.08 µm/m-°C @Temperature 24.0 - 300 °C |
8.378 µin/in-°F @Temperature 75.2 - 572 °F |
Mean |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Forged Disc, 2 Part Heat Treatment Tensile strength (ultimate and yield), reduction of area, and elongation values reported here are typical for Forged Disc, 2 Part Heat Treatment samples. Density and magnetic permeability are typica.. |
|||
CTE, linear | 15.08 µm/m-°C @Temperature 24.0 - 300 °C |
8.378 µin/in-°F @Temperature 75.2 - 572 °F |
Mean |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Forged Disc, 3 Part Heat Treatment Tensile strength (ultimate and yield), reduction of area, and elongation values reported here are typical for Forged Disc, 3 Part Heat Treatment samples. Density and magnetic permeability are typica.. |
|||
CTE, linear | 15.08 µm/m-°C @Temperature 24.0 - 300 °C |
8.378 µin/in-°F @Temperature 75.2 - 572 °F |
Mean |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Forged Disc, Solution Treated Tensile strength (ultimate and yield), reduction of area, and elongation values reported here are typical for Forged Disc, Solution Treated samples. Density and magnetic permeability are typical of .. |
|||
CTE, linear | 15.08 µm/m-°C @Temperature 24.0 - 300 °C |
8.378 µin/in-°F @Temperature 75.2 - 572 °F |
Mean |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Flat, 2 Part Heat Treatment, 1.250 inch (31.8 mm) Thickness Tensile strength (ultimate and yield), shear strength, compressive strength, reduction of area, and elongation values reported here are typical for Hot Finished Flat, 2 Part Heat Treatment, 1.250 in.. |
|||
CTE, linear | 15.08 µm/m-°C @Temperature 24.0 - 300 °C |
8.378 µin/in-°F @Temperature 75.2 - 572 °F |
Mean |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 3 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter Tensile strength (ultimate and yield), shear strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 3 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter s.. |
|||
CTE, linear | 15.08 µm/m-°C @Temperature 24.0 - 300 °C |
8.378 µin/in-°F @Temperature 75.2 - 572 °F |
Mean |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diameter Tensile strength (ultimate and yield), compressive strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diamete.. |
|||
CTE, linear | 15.08 µm/m-°C @Temperature 24.0 - 300 °C |
8.378 µin/in-°F @Temperature 75.2 - 572 °F |
Mean |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 2 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness Tensile and bearing strengths (ultimate and yield) and elongation values reported here are typical for Cold Rolled Sheet, 2 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness samples. Density and m.. |
|||
CTE, linear | 15.08 µm/m-°C @Temperature 24.0 - 300 °C |
8.378 µin/in-°F @Temperature 75.2 - 572 °F |
Mean |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 2 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter Tensile strength (ultimate and yield), shear strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 2 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter s.. |