- Polymer Property : CTE, linear = 8.00 µin/in-°F
Polymer Property : CTE, linear = 8.00 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.4 µm/m-°C @Temperature <=149 °C |
8.00 µin/in-°F @Temperature <=300 °F |
ASTM E228 |
| Greene Tweed Arlon® 1555 PEEK, Carbon, Graphite Filled Arlon® is a tough, high-temperature, semi-crystalline, thermoplastic presenting a unique combination of mechanical, thermal, chemical and electrical properties. Greene, Tweed uses several proprie.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 600 °C |
8.00 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 230® alloy, 20% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 600 °C |
8.00 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 30.0 - 316 °C |
8.00 µin/in-°F @Temperature 86.0 - 601 °F |
|
| Haynes Hastelloy® G-30® alloy, all-weld metal, GTAW weld 3.2 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 30.0 - 316 °C |
8.00 µin/in-°F @Temperature 86.0 - 601 °F |
|
| Haynes Hastelloy® G-30® alloy, mill annealed HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged 1300 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged at 649°C (1200°F) for 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 425 °C |
8.00 µin/in-°F @Temperature 77.0 - 797 °F |
|
| Haynes HR-160® alloy plate, aged 4000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 425 °C |
8.00 µin/in-°F @Temperature 77.0 - 797 °F |
|
| Haynes HR-160® alloy, plate, aged 4000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 425 °C |
8.00 µin/in-°F @Temperature 77.0 - 797 °F |
|
| Haynes HR-160® alloy, plate, aged 8000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® C-4 alloy, all-weld metal, as welded, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 30.0 - 316 °C |
8.00 µin/in-°F @Temperature 86.0 - 601 °F |
|
| Haynes Hastelloy® G-30® alloy, 25.4 mm thick bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 30.0 - 316 °C |
8.00 µin/in-°F @Temperature 86.0 - 601 °F |
|
| Haynes Hastelloy® G-30® alloy, 50% cold rolled and 1 hour at 500°C, air cooled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 425 °C |
8.00 µin/in-°F @Temperature 77.0 - 797 °F |
|
| Haynes HR-160® alloy plate, aged 8000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 21.0 - 538 °C |
8.00 µin/in-°F @Temperature 69.8 - 1000 °F |
Mean; Annealed and Aged |
| Special Metals INCONEL® 718SPF™ Nickel Superalloy, Annealed Typical annealing - continuous process anneal, 1700°F (927°C) at 15 ft (4.57 m) per minute. This produces ASTM No. 12 grain size. Heat capacity, melting range, moduli, and Poisson's ratio re.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 1000 °C |
8.00 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| ATI Allegheny Ludlum Ohmaloy® 30 Resistance Alloy Ohmaloy 30 alloy is a moderately magnetic, ductile stainless steel having extremely high electrical resistivity. In addition to imparting high electrical resistivity, the aluminum content in these .. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® C-4 alloy, sheet, aged 100 hours at 899°C Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 21.0 - 600 °C |
8.00 µin/in-°F @Temperature 69.8 - 1110 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Sheet, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 21.0 - 600 °C |
8.00 µin/in-°F @Temperature 69.8 - 1110 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 760 °C |
8.00 µin/in-°F @Temperature 68.0 - 1400 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 600 °C |
8.00 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 230® alloy plate, 16000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 600 °C |
8.00 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 230® alloy, 50% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 25.0 - 600 °C |
8.00 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 14.4 µm/m-°C @Temperature 21.0 - 600 °C |
8.00 µin/in-°F @Temperature 69.8 - 1110 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Bar, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||