- Polymer Property : CTE, linear = 7.89 µin/in-°F
Polymer Property : CTE, linear = 7.89 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 500 °C |
7.89 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Kennametal Stellite Stellite® 19 Can be machined with carbide tipped tools, but when hardness exceeds Rc55 it is best to grind. Applications include cutting tools, bearing races, guide rolls, and nozzle discs. Excellent resistance .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 0.000 - 700 °C |
7.89 µin/in-°F @Temperature 32.0 - 1290 °F |
|
| Kennametal Stellite Stellite® 6K 12.7 or 22.2 mm plate 13.3 mm^3 volume loss--abrasive wear data. Applications include agitators, augers, ball mills, banbury mills, cams, crusher bearings, dryers, dry presses, dump cars, fans, filters, food machinery, g.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Carbon steel 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Multimet alloy 12.7 mm plate weldment Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Type 304 Stainless steel 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® W alloy, gas metal arc welds, as-welded Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® W alloy, gas tungsten arc welds, as-welded Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 700 °C |
7.89 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 282® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® alloy 188 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® alloy X 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.89 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| Kennametal Stellite Stellite® 4 Cobalt Chromium Alloy The higher tungsten content of Stellite alloy 4 gives improved high temperature properties and an increase in abrasive wear resistance over Stellite alloy 6, but not as good as Stellite alloy 12 or .. |
|||