- Polymer Property : CTE, linear = 14.2 µm/m-°C
Polymer Property : CTE, linear = 14.2 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Alloy 188/ Multimet alloy 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Carbon steel 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® W alloy, gas tungsten arc welds, aged 1000 hours at 650°C (1200°F) Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® W alloy, shielded metal arc welds, as-welded Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 700 °C |
7.89 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 282® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, cold rolled and 1050°C mill-annealed sheet Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® alloy 718 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® alloy X 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 600 °C |
7.89 µin/in-°F @Temperature 1110 °F |
|
| Bohler-Uddeholm BÖHLER M268 VMR® Plastic Mold Steel Description: HBÖHLER M268 VMR is a hardened and tempered plastic mould steel with excellent cleanliness for best polishability. The hardness is constant over the entire cross-section of the steel b.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 199 °C |
7.90 µin/in-°F @Temperature 68.0 - 390 °F |
|
| Carlson 2205 (UNS S31803) Duplex Stainless Steel General DescriptionCarlson Alloy 2205 is a second-generation, nitrogen-alloyed duplex stainless steel (ferritic-austenitic). It offers an excellent combination of both strength and corrosion resist.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 199 °C |
7.90 µin/in-°F @Temperature 68.0 - 390 °F |
|
| Carlson 2205 (UNS S32205) Duplex Stainless Steel General DescriptionCarlson Alloy 2205 is a second-generation, nitrogen-alloyed duplex stainless steel (ferritic-austenitic). It offers an excellent combination of both strength and corrosion resist.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 90.0 °C |
7.89 µin/in-°F @Temperature 68.0 - 194 °F |
|
| ATI Allegheny Ludlum Type 332 Stainless Steel, UNS N08800 Type 332 is a nickel and chromium austenitic stainless steel designed to resist oxidation and carburization at elevated temperatures. The nickel content, 32%, makes the alloy highly resistant both .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 30% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 1000 °C |
7.89 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| ATI Allegheny Ludlum ALFA-II™ Stainless Steel Type 406 Characteristics:superior oxidation resistance for the temperature range 1600°F-over 2200°F, high electrical resistivity, high resistance to sulfidation, high resistance to carburization. Applicat.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.89 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| Kennametal Stellite Stellite® 4 Cobalt Chromium Alloy The higher tungsten content of Stellite alloy 4 gives improved high temperature properties and an increase in abrasive wear resistance over Stellite alloy 6, but not as good as Stellite alloy 12 or .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 427 °C |
7.89 µin/in-°F @Temperature 800 °F |
|
| Special Metals UDIMET® alloy L-605 Co-Cr-W-Ni Alloy UDIMET® alloy L-605 (UNS R30605) is a solid solution strengthened cobalt-chromium-tungsten-nickel alloy with excellent high-temperature strength and excellent oxidation resistance to 2000°F (1093°.. |
|||