- Polymer Property : CTE, linear = 13.4 µm/m-°C
Polymer Property : CTE, linear = 13.4 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.4 µm/m-°C @Temperature 20.0 - 800 °C |
7.44 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Kennametal Stellite Stellite® 98M2 cast Adhesive wear test data P/M 0.58 Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 21.0 - 400 °C |
7.44 µin/in-°F @Temperature 69.8 - 752 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2025°F (1107°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 21.0 - 400 °C |
7.44 µin/in-°F @Temperature 69.8 - 752 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 21.0 - 538 °C |
7.44 µin/in-°F @Temperature 69.8 - 1000 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 0.000 - 400 °C |
7.44 µin/in-°F @Temperature 32.0 - 752 °F |
|
| Kennametal Stellite Stellite® 12 PM cast Applications: include vane plugs, fuel metering pins, spacer bushings, ball blanks (bearings), race blanks (bearings), diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wea.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 24.0 - 538 °C |
7.44 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| HP Alloys Alloy C-276, 20% Cold Worked 20% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 732°C/8hr/FC to 621°C/8hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 20.0 - 538 °C |
7.44 µin/in-°F @Temperature 68.0 - 1000 °F |
|
| ATI Allegheny Ludlum AL 276™ Nickel-Base Alloy, UNS N10276 AL 276 alloy is a nickel-chromium-iron-tungsten alloy which is among the most corrosion resistant of alloys currently available. The AL 276 alloy is widely used in the severest environments encount.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 30% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 21.0 - 400 °C |
7.44 µin/in-°F @Temperature 69.8 - 752 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Sheet, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 21.0 - 400 °C |
7.44 µin/in-°F @Temperature 69.8 - 752 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 21.0 - 538 °C |
7.44 µin/in-°F @Temperature 69.8 - 1000 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 21.0 - 538 °C |
7.44 µin/in-°F @Temperature 69.8 - 1000 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 21.0 - 400 °C |
7.44 µin/in-°F @Temperature 69.8 - 752 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Bar, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||
| CTE, linear | 13.4 µm/m-°C @Temperature 204 °C |
7.43 µin/in-°F @Temperature 400 °F |
|
| Special Metals UDIMET® alloy L-605 Co-Cr-W-Ni Alloy UDIMET® alloy L-605 (UNS R30605) is a solid solution strengthened cobalt-chromium-tungsten-nickel alloy with excellent high-temperature strength and excellent oxidation resistance to 2000°F (1093°.. |
|||