Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 500 °C |
7.11 µin/in-°F @Temperature 68.0 - 932 °F |
|
Kennametal Stellite Nucalloy® 488 High-Silicon Nickel-Base Hardfacing Alloy Nucalloy® alloys are unique, patented, high-silicon, nickel-base hardfacing alloys that are designed to have optimum combinations of hardness and toughness, similar to the cobalt base alloys . B.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 0.000 - 200 °C |
7.11 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 12 PM with P/M Processing Applications: include vane plugs, fuel metering pins, spacer bushings, ball blanks (bearings), race blanks (bearings), diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wea.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 100 °C |
7.11 µin/in-°F @Temperature 68.0 - 212 °F |
|
Kennametal Stellite Stellite® 19 Can be machined with carbide tipped tools, but when hardness exceeds Rc55 it is best to grind. Applications include cutting tools, bearing races, guide rolls, and nozzle discs. Excellent resistance .. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 30.0 - 200 °C |
7.10 µin/in-°F @Temperature 86.0 - 392 °F |
|
International Mold Steel PX5 Pre-Hardened Mold Steel (P20 Type) PX5 is a modified P20, high performance, high precision, mold steel. Unique Characteristics: Exceptionally clean steel with uniform microstructure – no pin holes, inclusions or hard spots. 30-3.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 300 °C |
7.11 µin/in-°F @Temperature 68.0 - 572 °F |
|
Industeel Superplast® SP300 Prehardened Mold Steel Superplast® 300 (SP300) is a prehardened steel with a BHN 300 (32 HRC) to be used for plastic injection molds, extrusion dies, and compression molds offering improved performance for the mold mak.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 316 °C |
7.11 µin/in-°F @Temperature 68.0 - 601 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 316 °C |
7.11 µin/in-°F @Temperature 68.0 - 601 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 316 °C |
7.11 µin/in-°F @Temperature 68.0 - 601 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 316 °C |
7.11 µin/in-°F @Temperature 68.0 - 601 °F |
|
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 25.0 - 100 °C |
7.11 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 25.0 - 100 °C |
7.11 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 625 alloy, 40% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 25.0 - 100 °C |
7.11 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 25.0 - 100 °C |
7.11 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 427 °C |
7.11 µin/in-°F @Temperature 69.8 - 801 °F |
0.20%C |
Latrobe CBS-600™ VIM-VAR Carburizing Bearing and Gear Steel CBS-600 VIM-VAR is a carburizing bearing and gear steel designed for service temperatures up to 600°F. Double vacuum melting is employed to provide optimum tensile properties as well as describe.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 23.9 - 316 °C |
7.11 µin/in-°F @Temperature 75.0 - 600 °F |
|
HP Alloys Alloy C-276, 20% Cold Worked 20% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 100 °C |
7.11 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 10% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 100 °C |
7.11 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 50% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of .. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 100 °C |
7.11 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) + Aged 1400°F (760°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 1950°F (1070°C)/5 minutes/AC + Aged 1400°F (760°C)/100h/AC. This produces ASTM grain siz.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 21.1 - 302 °C |
7.10 µin/in-°F @Temperature 70.0 - 575 °F |
|
Schmolz + Bickenbach P-20 High Hard Plastic Mold Steel Description: P-20 High Hard is an improved pre-hardened mold steel that has been specially designed for large plastic molds; Material is forged on a 5000 ton press assuring maximum deformation durin.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 21.1 - 302 °C |
7.10 µin/in-°F @Temperature 70.0 - 575 °F |
|
Schmolz + Bickenbach P-20 Modified Plastic Mold Steel Description: P-20 Modified is an improved pre-hardened mold steel that has been specially designed for large plastic molds; The material is forged on a 5000 ton press assuring maximum deformation du.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 21.1 - 316 °C |
7.10 µin/in-°F @Temperature 70.0 - 600 °F |
|
Crucible Steel CSM® 21 17Cr-4Ni Precipitation Hardening Stainless Steel CSM 21 is a precipitation hardening stainless mold steel, providing outstanding corrosion resistance and toughness, good polishability, and moderate wear resistance, combined with simple heat treatm.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 21.1 - 204 °C |
7.10 µin/in-°F @Temperature 70.0 - 400 °F |
|
Crucible Steel Nitriding #135 Modified Steel, AISI 4140 Modified Nitriding #135 steel is a modification of AISI 4140 specifically designed to be nitrided for high surface hardness and abrasion resistance.Information provided by Crucible Industries |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 93.0 °C |
7.11 µin/in-°F @Temperature 69.8 - 199 °F |
|
Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 0% Cold Reduction Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 93.0 °C |
7.11 µin/in-°F @Temperature 69.8 - 199 °F |
|
Carpenter MP35N* Ni-Co-Cr-Mo Alloy, Cold Drawn 33%, Aged 565°C/4hr/AC Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 93.0 °C |
7.11 µin/in-°F @Temperature 68.0 - 199 °F |
|
ATI Allegheny Ludlum Altemp® 718 Nickel-Base Superalloy, Solution Treated Sheet and Strip, UNS N07718 Allegheny Ludlum Altemp 718 alloy is an austenitic nickel-base superalloy which is used in applications requiring high strength to approximately 760 degrees Celsius and oxidation resistance to appro.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 600 °C |
7.11 µin/in-°F @Temperature 68.0 - 1110 °F |
|
ATI Allegheny Ludlum Martensitic Stainless Steel Type 425 Mod, Hardened + 538°C Temper Allegheny Ludlum Type 425 Mod is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stai.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 25.0 - 100 °C |
7.11 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 316 °C |
7.11 µin/in-°F @Temperature 68.0 - 601 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 25.0 - 100 °C |
7.11 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 100 °C |
7.11 µin/in-°F @Temperature 68.0 - 212 °F |
|
Kennametal Stellite Stellite® 4 Cobalt Chromium Alloy The higher tungsten content of Stellite alloy 4 gives improved high temperature properties and an increase in abrasive wear resistance over Stellite alloy 6, but not as good as Stellite alloy 12 or .. |