Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 12.7 µm/m-°C @Temperature 20.0 - 600 °C |
7.06 µin/in-°F @Temperature 68.0 - 1110 °F |
|
Kennametal Stellite Nucalloy® 488V High-Silicon Nickel-Base Hardfacing Alloy Applications include diesel engine valves, and injection mold screws.Nucalloy® alloys are unique, patented, high-silicon, nickel-base hardfacing alloys that are designed to have optimum combinati.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 230® alloy, 40% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 230® alloy, plate, 4000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 600 °C |
7.06 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Bar, Hot Rolled and Solution Annealed HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 500 °C |
7.06 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 21.0 - 427 °C |
7.06 µin/in-°F @Temperature 69.8 - 801 °F |
|
Haynes Hastelloy® N, weld metal as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 300 °C |
7.06 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 263® alloy, cold rolled sheet, solution treated and aged Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.06 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.06 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Sheet Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.06 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Plate, Annealed Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.06 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Sheet, Cold-rolled, Solution Annealed, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.06 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 21.0 - 204 °C |
7.06 µin/in-°F @Temperature 69.8 - 399 °F |
0.20%C |
Latrobe CBS-600™ VIM-VAR Carburizing Bearing and Gear Steel CBS-600 VIM-VAR is a carburizing bearing and gear steel designed for service temperatures up to 600°F. Double vacuum melting is employed to provide optimum tensile properties as well as describe.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 600 °C |
7.06 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 20.0 - 500 °C |
7.06 µin/in-°F @Temperature 68.0 - 932 °F |
|
Bohler-Uddeholm BÖHLER S601 (M2 Modified) High Speed Steel For Cold Work Applications Properties: Tungs ten-molybdenum high speed steel with ex cel lent toughness and cut ting proper ties, for a wide variety of uses.Applications: Taps, twist drills, reamers, broaching tools, meta.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 500 °C |
7.06 µin/in-°F @Temperature 932 °F |
|
Bohler-Uddeholm BÖHLER S692/S693 MICROCLEAN® PM M4 High Speed Steel Description: S692/S693 MICROCLEAN are high-sulfur and low sulfur versions of high-carbon PM M4 high speed steel that is produced using state-of-the-art “Generation 3” powder processing technology... |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 20.0 - 400 °C |
7.06 µin/in-°F @Temperature 68.0 - 752 °F |
|
Assab Steels DIEVAR Hot Work Steel DIEVAR is a high performance chromium-molybdenum-vanadium alloyed hot work tool steel which offers a very good resistance to heat checking, gross checking, hot wear and plastic deformation. DIEVAR i.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 500 °C |
7.06 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing spe.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 21.0 - 427 °C |
7.06 µin/in-°F @Temperature 69.8 - 801 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 21.0 - 427 °C |
7.06 µin/in-°F @Temperature 69.8 - 801 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 230® alloy plate, 8000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 230® alloy, plate, 4000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 12.7 µm/m-°C @Temperature 21.0 - 427 °C |
7.06 µin/in-°F @Temperature 69.8 - 801 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |