- Polymer Property : CTE, linear = 12.3 µm/m-°C
Polymer Property : CTE, linear = 12.3 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.3 µm/m-°C @Temperature 0.000 - 100 °C |
6.83 µin/in-°F @Temperature 32.0 - 212 °F |
|
| Kennametal Stellite Stellite® 3 PM cast Typical applications include (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) diesel engine exhaust, fluid valve seats, saw cutt.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 600 °C |
6.83 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed, 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 21.0 - 100 °C |
6.83 µin/in-°F @Temperature 69.8 - 212 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2025°F (1107°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 21.0 - 100 °C |
6.83 µin/in-°F @Temperature 69.8 - 212 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 600 °C |
6.83 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 242® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 600 °C |
6.83 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 242® alloy, after 8000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 600 °C |
6.83 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, room temperature sheet after 100 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, room temperature sheet after 1000 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, room temperature sheet after 1000 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 21.1 - 538 °C |
6.85 µin/in-°F @Temperature 70.0 - 1000 °F |
|
| Latrobe BG42® Stainless Knife Steel (AMS 5749) LESCALLOY® BG42® VIM VAR is a double vacuum melted martensitic stainless high speed steel designed for critical aerospace structural components and high performance bearings. The steel is vacu.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 20.0 - 500 °C |
6.83 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Latrobe DuraTechâ„¢ 20CV Powder Metal Stainless Tool Steel DuraTech 20CV is a highly wear resistant, powder metallurgy stainless tool steel. The steel contains a large volume of extremely hard vanadium carbides, which provide excellent wear resistance. Du.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 21.0 - 100 °C |
6.83 µin/in-°F @Temperature 69.8 - 212 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 37.8 - 649 °C |
6.82 µin/in-°F @Temperature 100 - 1200 °F |
|
| Crucible Steel REX® M4 High Speed Steel REX M4 is a special purpose high speed steel designed to give high wear resistance in tools. Its high vanadium and carbon content provide for high resistance to cratering and wear in cold work punch.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 20.0 - 299 °C |
6.83 µin/in-°F @Temperature 68.0 - 570 °F |
|
| Bohler-Uddeholm BÖHLER K340 ISODUR® Premium Cold Work Steel BÖHLER K340 ISODUR is a universal cold work tool steel with which you‘ll be making money and just when blanking coins, but also when: blanking, cutting, cold rolling, extruding, deep drawing and b.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 400 °C |
6.83 µin/in-°F @Temperature 752 °F |
|
| Bohler-Uddeholm BÖHLER S400(M7) High Speed Steel Description: High alloyed molybdenum high speed steel with good resistance and high toughness.Applications: Taps, twist drills, reamers, milling tools, broaches tools, cold extrusion dies.Standards:.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 400 °C |
6.83 µin/in-°F @Temperature 752 °F |
|
| Bohler-Uddeholm BÖHLER S401(M1) High Speed Steel Description: Molybdenum high speed steel with high toughness and good cutting ability. Applications: Taps, twist drills, reamers, milling tools, broaches toolsStandards: DIN/EN 1.3346 HS2-91, AISI M.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature -17.8 - 500 °C |
6.83 µin/in-°F @Temperature 0.000 - 932 °F |
|
| American Utility Metals Cromgard® Stainless Steel Cromgard is a low cost stainless steel, which is able to provide benefits of good weldability and formability, making it capable of fabrication by conventional techniques. It provides the benefits o.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 20.0 - 200 °C |
6.83 µin/in-°F @Temperature 68.0 - 392 °F |
Hardened and tempered to 56 HRC |
| Assab Steels CARMO Cold Work Steel CARMO is a high-strength, flame-induction and through hardening steel delivered prehardened to 240-270 HB.The surface of the steel can be flame-hardened without water cooling to a hardness of 58±2.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 50.0 °C |
6.83 µin/in-°F @Temperature 77.0 - 122 °F |
|
| Carpenter HyMu "80"® Electronic Alloy, Strip, After Process Anneal Data provided by Carpenter Technology Corporation.Carpenter HyMu “80” ® alloy is an unoriented, 80% nickel-iron-molybdenum alloy which offers extremely high initial permeability as well as maximu.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 21.0 - 316 °C |
6.83 µin/in-°F @Temperature 69.8 - 601 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 21.0 - 316 °C |
6.83 µin/in-°F @Temperature 69.8 - 601 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||