Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Transverse to Flow | 50.0 - 100 µm/m-°C | 27.8 - 55.6 µin/in-°F | Average value: 79.3 µm/m-°C Grade Count:15 |
Overview of materials for Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant". Each property range of values re.. |
|||
CTE, linear, Transverse to Flow | 85.0 - 100 µm/m-°C | 47.2 - 55.6 µin/in-°F | Average value: 91.7 µm/m-°C Grade Count:3 |
Overview of materials for Polycyclohexylenedimethylene Terephthalate (PCT), 30% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PCT or PCTA, 30% Glass Reinforced".Specific grades with glass content between 25% and 34% are included. .. |
|||
CTE, linear, Transverse to Flow | 27.0 - 100 µm/m-°C | 15.0 - 55.6 µin/in-°F | Average value: 51.2 µm/m-°C Grade Count:10 |
Overview of materials for Acetal Copolymer, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Carbon Fiber Filled". Each property range of values reported is minimum and maximum va.. |
|||
CTE, linear, Transverse to Flow | 3.60 - 100 µm/m-°C | 2.00 - 55.6 µin/in-°F | Average value: 63.6 µm/m-°C Grade Count:9 |
Overview of materials for Acetal Homopolymer, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, Glass Fiber Reinforced". Each property range of values reported is minimum and maxim.. |
|||
CTE, linear, Transverse to Flow | 76.0 - 100 µm/m-°C @Temperature 55.0 - 260 °C |
42.2 - 55.6 µin/in-°F @Temperature 131 - 500 °F |
Average value: 83.8 µm/m-°C Grade Count:4 |
Overview of materials for Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled". Specific grades with glass content between 45% an.. |
|||
CTE, linear, Transverse to Flow | 76.0 - 100 µm/m-°C @Thickness 2.00 - 4.00 mm |
42.2 - 55.6 µin/in-°F @Thickness 0.0787 - 0.157 in |
Average value: 83.8 µm/m-°C Grade Count:4 |
Overview of materials for Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled". Specific grades with glass content between 45% an.. |
|||
CTE, linear, Transverse to Flow | 34.0 - 100 µm/m-°C | 18.9 - 55.6 µin/in-°F | Average value: 66.3 µm/m-°C Grade Count:24 |
Overview of materials for Nylon 6, Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass/Mineral Reinforced". Each property range of values reported is minimum and maximum values.. |
|||
CTE, linear, Transverse to Flow | 50.0 - 100 µm/m-°C | 27.8 - 55.6 µin/in-°F | Average value: 75.3 µm/m-°C Grade Count:8 |
Overview of materials for Nylon 66, Glass/Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass/Mineral Filled". Each property range of values reported is minimum and maximum values of.. |
|||
CTE, linear, Transverse to Flow | 60.0 - 100 µm/m-°C @Temperature 23.0 - 80.0 °C |
33.3 - 55.6 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 11359-1/-2 |
BASF Ultramid® C3U BK 23079 PA6/66 FR (Conditioned) Description: Injection-molding grade with improved flame retardance (free from halogens and phosphorus), used e.g. for impact resistant electrically insulating parts such as contact bases and plug c.. |
|||
CTE, linear, Transverse to Flow | 70.0 - 100 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 - 55.6 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 11359-1/-2 |
BASF Ultramid® FRee A3U40G5 25% Glass Filled PA66 FR (Dry) Description: Flame retardant without halogens and red phosphorus, 25% glass fiber reinforced injection-molding grade; light colorable; outstanding mechanical and electrical properties.Information pr.. |
|||
CTE, linear, Transverse to Flow | 35.0 - 100 µm/m-°C | 19.4 - 55.6 µin/in-°F | Average value: 68.7 µm/m-°C Grade Count:7 |
Overview of materials for Polyethylene Terephthalate (PET), 50% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 50% Glass Reinforced". Specific grades with glass content between 45% .. |
|||
CTE, linear, Transverse to Flow | 22.0 - 100 µm/m-°C @Temperature -100 - 250 °C |
12.2 - 55.6 µin/in-°F @Temperature -148 - 482 °F |
Average value: 81.8 µm/m-°C Grade Count:23 |
Overview of materials for Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS)- 40% Glass filled; Molded". Specific grades with glass content between 35% a.. |