Thermal Properties | Metric | English | Comments |
---|---|---|---|
Glass Transition Temp, Tg | 144 °C | 291 °F | DSC |
Solvay Specialty Polymers Kalix® 3850 Polyamide, High Performance (HPPA), 50% Glass Fiber Kalix® 3850 is a 16% bio-sourced, amorphous polyphthalamide (PPA)-based compound with 50% by weight glass fiber reinforcement. This material is uniquely formulated to prevent warpage and flash in.. |
|||
Glass Transition Temp, Tg | 144 °C | 291 °F | DSC |
Solvay Specialty Polymers Kalix® 3950 Polyamide, High Performance (HPPA), 50% Glass Fiber Kalix® 3950 is a 16% bio-sourced, amorphous polyphthalamide (PPA)-based compound with 50% by weight glass fiber reinforcement. This material is uniquely formulated to prevent warpage and flash in.. |
|||
Glass Transition Temp, Tg | 144 °C | 291 °F | 10°C/min; ISO 11357-1,-2 |
Covestro Makrolon® 1952 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardancy• Me.. |
|||
Glass Transition Temp, Tg | 144 °C | 291 °F | ISO 11357-1/-2 |
Covestro Makrolon® 2467 Polycarbonate ISO 7391-PC,MFLR,(,,)-18-9Global gradeFormerly Makrolon DP1-1870MVR (300 °C/1.2 kg) 19 cm3/10 minChlorine- and bromine-free flame retardantUL 94V-2/1.5 mm and 3.0 mmLow viscosityUV stabilizedEasy r.. |
|||
Glass Transition Temp, Tg | 144 °C | 291 °F | 10°C/min; ISO 11357-1,-2 |
Covestro Makrolon® 2607 MAS167 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Med.. |
|||
Glass Transition Temp, Tg | 144 °C | 291 °F | 10°C/min; ISO 11357-1,-2 |
Covestro Makrolon® 2665 MAS071 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardant• Med.. |
|||
Glass Transition Temp, Tg | 144 °C | 291 °F | 10°C/min; ISO 11357-1,-2 |
Covestro Makrolon® 2665 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medium viscosity, easy.. |
|||
Glass Transition Temp, Tg | 144 °C | 291 °F | 10°C/min; ISO 11357-1,-2 |
Covestro Makrolon® 2667 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardant• Med.. |
|||
Glass Transition Temp, Tg | 144 °C | 291 °F | ISO 11357-1/-2 |
Covestro Makrolon® 2667 Polycarbonate, Flame Retardant Grade ISO 7391-PC,MFLR,(,,)-18-9Global gradeMVR (300 °C/1.2 kg) 12.5 cm3/10 minChlorine- and bromine-free flame retardantUL 94V-2/1.5 mm and 3.0 mmMedium viscosityUV stabilizedEasy releaseInjection moldi.. |
|||
Glass Transition Temp, Tg | 144 °C | 291 °F | ISO 11357-1/-2 |
Covestro Makrolon® 2867 Polycarbonate, Flame Retardant Grade ISO 7391-PC,MFLR,(,,)-09-9MVR (300 °C/1.2 kg) 9.5 cm3/10 minChlorine- and bromine-free flame retardantUL 94V-2/1.5 mm and 3.0 mmMedium viscosityUV stabilizedEasy releaseInjection molding - Melt tem.. |
|||
Glass Transition Temp, Tg | 144 °C | 291 °F | ISO 11357-1/-2 |
Covestro Makrolon® 6357 Polycarbonate, Flame Retardant Grade ISO 7391-PC,MFLR,(,,)-18-9MVR (300 °C/1.2 kg) 14.5 cm3/10 minChlorine- and bromine-free flame retardantUL 94V-0/3.0 mmMedium viscosityUV stabilizedEasy releaseInjection molding - Melt temperature 2.. |
|||
Glass Transition Temp, Tg | 144 °C | 291 °F | ISO 11357-1/-2 |
Covestro Makrolon® 6457 Polycarbonate, Flame Retardant Grade MVR (300 °C/1.2 kg) 12.5 cm3/10 minUL 94V-0/3.0 mmUV stabilizedeasy releaseinjection moldingavailable in transparent, translucent and opaque colorsPreprocessingMax. Water content |
|||
Glass Transition Temp, Tg | 144 °C | 291 °F | ISO 11357-1/-2 |
Covestro Makrolon® AG2677 Polycarbonate ISO 7391-PC,MLR,(,,)-18-9Global gradeMVR (300 °C/1.2 kg) 12.5 cm3/10 minMedium viscosityUV stabilizedEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable in transparent colors on.. |
|||
Glass Transition Temp, Tg | 144 °C | 291 °F | ISO 11357-1/-2 |
Covestro Makrolon® AL2447 Polycarbonate ISO 7391-PC,MLR,(,,)-18-9Global gradeMVR (300 °C/1.2 kg) 19 cm3/10 minAutomotive lightingLow viscosityUV stabilizedEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable in transpa.. |
|||
Glass Transition Temp, Tg | 144 °C | 291 °F | |
Armstrong A-702 Epoxy Adhesive Information provided by Ellsworth Adhesives. |
|||
Glass Transition Temp, Tg | 144 °C | 291 °F | 10°C/min; ISO 11357-1,-2 |
Covestro Makrolon® LQ2647 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Optical lens, safety g.. |
|||
Glass Transition Temp, Tg | 144 °C | 291 °F | ISO 11357-1/-2 |
Covestro Makrolon® LQ2687 Polycarbonate ISO 7391-PC,MLR,(,,)-18-9MVR (300 °C/1.2 kg) 12.5 cm3/10 minOptical lensMedium viscosityUV stabilizedUV 400 cut offEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable in clear t.. |