Thermal Properties | Metric | English | Comments |
---|---|---|---|
Glass Transition Temp, Tg | 187 °C | 369 °F | ASTM D3482 |
Gharda Chemicals Gafone S 1320GF Polysulfone (PS)
(discontinued **) Characteristics: High Temperature Resistance - Tg 189°C Excellent Clarity Excellent Mechanical & Electrical properties Easy to process Very good Hydrolytic Resistance Applications: Elec.. |
|||
Glass Transition Temp, Tg | 187 °C | 369 °F | ASTM D3482 |
Gharda Chemicals Gafone S S1430SP60 Polysulfone (PS)
(discontinued **) Characteristics: High Temperature Resistance - Tg 189°C Excellent Clarity Excellent Mechanical & Electrical properties Easy to process Very good Hydrolytic Resistance Applications: Elec.. |
|||
Glass Transition Temp, Tg | 187 °C | 369 °F | ISO 11357-1/-3 |
BASF Ultrason S 2010 G4 20% Glass Filled PSU Ultrason S 2010 G4 is a 20% glass reinforced, medium viscosity injection molding PSU grade with high rigidity and strength. |
|||
Glass Transition Temp, Tg | 187 °C | 369 °F | ISO 11357-1/-3 |
BASF Ultrason S 2010 PSU Ultrason S 2010 is an unreinforced, medium viscosity standard injection molding PSU grade. It flows readily and offers outstanding heat resistance and dimensional stability. It conforms to FDA req.. |
|||
Glass Transition Temp, Tg | 187 °C | 369 °F | ISO 11357-1/-2 |
BASF Ultrason® S 3010 MR UN PSU Description: Unreinforced, higher viscosity injection molding and extrusion grade, tougher, with improved chemical resistance and demolding optimized. Abbreviated designation according to ISO 1043-1.. |
|||
Glass Transition Temp, Tg | 187 °C | 369 °F | ASTM D3482 |
Gharda Chemicals Gafone S 1500 Polysulfone (PS)
(discontinued **) Characteristics: High Temperature Resistance - Tg 189°C Excellent Clarity Excellent Mechanical & Electrical properties Easy to process Very good Hydrolytic Resistance Applications: Elec.. |
|||
Glass Transition Temp, Tg | 187 °C | 369 °F | 10 K/min; ISO 11357-1/-3 |
BASF Ultrason S 6010 PSU Ultrason S 6010 is an unreinforced, high molecular weight injection-molding and extrusion grade with excellent chemical resistance (stress crack resistance) and good solubility in typical solvents (.. |
|||
Glass Transition Temp, Tg | 187 - 265 °C | 369 - 509 °F | Average value: 232 °C Grade Count:3 |
Overview of materials for Polysulfone, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are inc.. |