Polymer Property : Specific Heat Capacity = 0.155 BTU/lb-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.647 J/g-°C @Temperature 700 °C |
0.155 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1200°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.647 J/g-°C @Temperature 700 °C |
0.155 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes HR-120® alloy, solution heat-treated plate Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Specific Heat Capacity | 0.650 J/g-°C | 0.155 BTU/lb-°F | |
| Schott LLF1 Glass Information Provided by SCHOTT North America, Inc. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Specific Heat Capacity | 0.648 J/g-°C @Temperature 1000 °C |
0.155 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||