- Polymer Property : Specific Heat Capacity = 0.143 BTU/lb-°F
Polymer Property : Specific Heat Capacity = 0.143 BTU/lb-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 20.0 - 100 °C |
0.143 BTU/lb-°F @Temperature 68.0 - 212 °F |
DINV ENV 821-3 |
| CeramTec CD 101 Silicon Carbide, SiC-ZrB2 CD101 is a zirconia reinforced silicon carbide designed for maximum hardness. |
|||
| Specific Heat Capacity | 0.600 J/g-°C | 0.143 BTU/lb-°F | DINV ENV 821-3 |
| CeramTec CD 110 Silicon Carbide, SSiC Silicon carbide is extremely hard and displays excellent corrosion and thermal shock resistance. It outstanding sliding properties and high thermal conductivity make useful in tribological applicati.. |
|||
| Specific Heat Capacity | 0.600 J/g-°C | 0.143 BTU/lb-°F | DINV ENV 821-3 |
| CeramTec Rocar® ST Silicon Carbide, SSiC Silicon carbide is extremely hard and displays excellent corrosion and thermal shock resistance. Its outstanding sliding properties and high thermal conductivity make useful in tribological applicat.. |
|||
| Specific Heat Capacity | 0.600 J/g-°C | 0.143 BTU/lb-°F | ASTM E1269 |
| CoorsTek TTZ (Dura-Z™) MgO Partially Stabilized Zirconia Thermal Shock Delta Tc = 350°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 30% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Specific Heat Capacity | 0.600 J/g-°C @Temperature 800 °C |
0.143 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||