- Polymer Property : Specific Heat Capacity = 0.107 BTU/lb-°F
Polymer Property : Specific Heat Capacity = 0.107 BTU/lb-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 20.0 °C |
0.107 BTU/lb-°F @Temperature 68.0 °F |
|
| Hoskins Manufacturing Chromel® Thermocouple Wire Used in Type E and Type K thermocouples. All values may vary dependent on specific design and usageChromel® is a registered trade name of Hoskins Manufacturing.Capabilities: WireRibbonSquareInsu.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, 30% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, plate, 4000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C | 0.107 BTU/lb-°F | |
| Latrobe Lescalloy® 300M VAC-ARC High Strength Alloy Steel LESCALLOY 300M VAC-ARC steel is a modified 4340 steel with added silicon allowing for use of a higher tempering temperature. The steel has high hardenability and strength with good ductility and tou.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C | 0.107 BTU/lb-°F | |
| Latrobe Lescalloy® 4340 VAC-ARC ; 3.5" round High Strength Alloy Steel LESCALLOY 4340 VAC-ARC steel is a low alloy, nickel-chromium-molybdenum steel capable of being heat treated to high strength levels. The alloy has a good combination of ductility, toughness and str.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C | 0.107 BTU/lb-°F | |
| Latrobe Lescalloy® 4340 VAC-ARC ; 10.5" square High Strength Alloy Steel LESCALLOY 4340 VAC-ARC steel is a low alloy, nickel-chromium-molybdenum steel capable of being heat treated to high strength levels. The alloy has a good combination of ductility, toughness and str.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C | 0.107 BTU/lb-°F | |
| Special Metals INCONEL® 601GC® Nickel Superalloy Data provided by the manufacturer, Special Metals. |
|||
| Specific Heat Capacity | 0.448 J/g-°C | 0.107 BTU/lb-°F | |
| Special Metals INCONEL® Alloy 601 A nickel-chromium alloy with an addition of aluminum for outstanding resistance to oxidation and other forms of high-temperature corrosion. It also has high mechanical properties at elevated temper.. |
|||
| Specific Heat Capacity | 0.446 J/g-°C | 0.107 BTU/lb-°F | |
| Special Metals NIMONIC® Alloy 90 A precipitation-hardenable nickel-chromium-cobalt alloy having high stress-rupture strength and creep resistance at temperatures to about 1700°F (920°C). The alloy also has good resistance to.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, GMAW deposit weld metal Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy plate, 16000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, 50% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, as cast vacuum investment casting Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Specific Heat Capacity | 0.448 J/g-°C @Temperature 300 °C |
0.107 BTU/lb-°F @Temperature 572 °F |
|
| Haynes 230® alloy, plate, 4000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||