Thermal Properties | Metric | English | Comments |
---|---|---|---|
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, 20% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, 30% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, 30% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, 30% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, plate, 4000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 200 °C |
0.100 BTU/lb-°F @Temperature 392 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed, 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 200 °C |
0.100 BTU/lb-°F @Temperature 392 °F |
|
Haynes 242® alloy, after 1000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 200 °C |
0.100 BTU/lb-°F @Temperature 392 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Specific Heat Capacity | 0.419 J/g-°C | 0.100 BTU/lb-°F | |
Special Metals BRIGHTRAY® Alloy C Electrical Resistance Alloy A nickel-chromium electrical-resistance alloy for use at operating temperatures up to 2100°F (1150°C). It contains rare-earth additions for increased oxidation resistance, especially under co.. |
|||
Specific Heat Capacity | 0.419 J/g-°C | 0.100 BTU/lb-°F | |
Special Metals BRIGHTRAY® Alloy S Electrical Resistance Alloy A nickel-chromium electrical-resistance alloy for use at temperatures up to 2100°F (1150°C) under continuous operating conditions. It is similar to BRIGHTRAY alloy C but does not contain rare.. |
|||
Specific Heat Capacity | 0.419 J/g-°C | 0.100 BTU/lb-°F | |
Special Metals MONEL® Alloy K-500 A precipitation-hardenable nickel-copper alloy that combines the corrosion resistance of MONEL alloy 400 with greater strength and hardness. It also has low permeability and is nonmagnetic to under.. |
|||
Specific Heat Capacity | 0.419 J/g-°C | 0.100 BTU/lb-°F | |
Special Metals NIMONIC® Alloy PK33 A nickel-chromium-cobalt alloy that is precipitation hardenable and also contains a relatively high (7%) level of molybdenum for solid-solution strengthening. It has an exceptional combination of h.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 0.000 - 100 °C |
0.100 BTU/lb-°F @Temperature 32.0 - 212 °F |
condition H 900 |
Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 1100 (Heated 593°C) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 0.000 - 100 °C |
0.100 BTU/lb-°F @Temperature 32.0 - 212 °F |
condition H 900 |
Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 1150M (Heated 760°C/2hr/AC then 621°C/4hr/AC) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, GMAW deposit weld metal Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 0.000 - 100 °C |
0.100 BTU/lb-°F @Temperature 32.0 - 212 °F |
condition H 900 |
Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 1025 (Heated 552°C) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy plate, 16000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, as cast vacuum investment casting Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, plate, 4000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |